Abstract:The microstructure and mechanical characteristics of the AZ61 magnesium alloy with varying RE (RE) content during the extrusion-forging process were thoroughly examined using metallography, SEM, EDS, and XRD. Findings indicate that as the RE content increases, the β-Mg 17 Al 12 phase is significantly diminished, primarily resulting in a microstructure composed of Al 4 Ce and Al 8 Mn 4 Ce phases or Al 3 Nd and Al 4 Ce phases, along with a minor presence of Al 4 La phase, which appears in black granular or agglomerated forms along the extrusion axis. Following die forging, the RE phases in the AZ61+xRE Mg alloy's microstructure experienced secondary fragmentation due to triaxial compressive stress, leading to a drum-shaped or S-shaped distribution of the fractured RE material, without any spheroidization or new phase formation occurring during deformation, while the β-Mg 17 Al 12 phase was entirely dissolved in the matrix. Post die forging, the mechanical properties of the AZ61+xRE magnesium alloy showed significant enhancement, with the AEZ641 alloy exhibiting the highest increases in tensile strength and yield strength, at 8.5 and 26.2%, respectively. Nonetheless, the elongation of all four alloys decreased markedly, by 42 to 52%, and hardness increased by 3.5 to 7.1%. As RE content rose, the yield strength, tensile strength, elongation, and hardness of the as-forged AEZ611 alloy reached values of 220 MPa, 302.3 MPa, 11.25%, and 65.8 HRE, respectively, showcasing the best overall mechanical properties at room temperature. During the transition from extrusion to die forging, the macrofracture exhibited distinct necking, while the microfracture revealed numerous pits, with a significant presence of second phase or RE particles located at the pits' bottoms. The fracture mechanism was identified as a mixed fracture with characteristics of toughness.

Hot deformation behavior of an extruded AZ31 alloy doped with rare-earth elements

Effect of Double Plastic Deformation on Microstructure and Mechanical Properties of High-Content Rare-Earth AZ61 Mg Alloy

Synergistic Effects of Cerium-Based Rare Earth Addition and Hot Deformation on the Microstructure and Mechanical Properties of Mg-0.5Zn-0.5Zr Magnesium Alloy

Microstructural evolution and dynamic recrystallization model of extruded homogenized AZ31 magnesium alloy during hot deformation

Analysis of high-temperature deformation and microstructure of an AZ31 magnesium alloy

Effect of Zr and Er Addition on the Microstructural Evolution of a Novel Al−Mg−Zn−Er−Zr Alloy during Hot Compression

Effect of microalloying with Ca and Gd on the hot deformation behavior of AZ31 alloy

Deformation Behavior and Microstructure Evolution of AZ31 Mg Alloy by Forging–Bending Repeated Deformation with Multi-pass Lowered Temperature

Influence of rare earth addition on microstructures and mechanical properties of high-pressure die casting Mg–8Zn–6Al alloy

Processing Maps and Hot Compression Behaviors of ZK60 Alloy After Adding Different Rare Earth Elements

Varying strain rates and elevated temperatures effects on the mechanical properties of AZ31B magnesium alloy

Hot deformation behavior of novel high-strength Mg-0.6Mn-0.5Al-0.5Zn-0.4Ca alloy

Study on the Microstructure and Properties of AZ31 Alloy by Hot Die Forging Extrusion

Hot Deformation Behavior and Processing Map of Coarse-Grained Mg–Gd–Y–Nd–Zr Alloy

Analysis of hot deformation behavior and processing map of extruded AZ40 alloy

Modification of the Tensile Performance of an Extruded ZK60 Magnesium Alloy with the Addition of Rare Earth Elements

Effects of extrusion ratio and temperature on the microstructure and mechanical properties of Mg–Zn–Yb–Zr extrusion alloys

Investigation of the optimum preheating treatment parameters for extruded Mg–Gd–Y–Zn–Zr alloy using high-throughput experiments

Study on Hot Deformation Behavior of Mg-9Y-1MM-1Zn-0.6Zr Alloy

Characterization of Hot Deformation Behavior and Processing Maps of Homogenized Al-Mg-Si-Sc-Zr Alloys

Hot Deformation Behaviors of AZ91 Magnesium Alloy: Constitutive Equation, Ann-Based Prediction, Processing Map and Microstructure Evolution