Metal oxide sol annealing on perovskite MAPbI3 film with thermal stability enhanced by caffeine additive and PMMA interlayer

Yew Hang Soo,Chai Yan Ng,Hieng Kiat Jun,Soo Ai Ng,Yew Hoong Wong

DOI: https://doi.org/10.1007/s10853-022-07335-0

IF: 4.5

2022-06-03

Journal of Materials Science

Abstract:Methylammonium lead iodide (MAPbI 3 ) is a popular light-absorbing layer in the perovskite solar cells (PSCs). However, the poor thermal stability of MAPbI 3 has inhibited the direct annealing of low-temperature processed (≤ 150 °C) metal oxide sols as a charge transport layer (CTL) on top of it. In this work, caffeine as a nonvolatile and low-cost additive was added into the poly(methyl methacrylate) (PMMA)-encapsulated MAPbI 3 film to enhance its thermal stability at 150 °C. The caffeine-added MAPbI 3 (C-MAPbI 3 ) film was prepared using antisolvent-assisted one-step spin-coating. With caffeine additive, the thermal degradation of the C-MAPbI 3 film was significantly reduced, and the film still retained dominating MAPbI 3 phase after 24 h of annealing. In addition, the caffeine additive improved the film morphology by promoting seamless grain boundary formation. The thickness of the PMMA encapsulation layer deposited on top of the C-MAPbI 3 film could be reduced from ~ 1550 nm (charge insulating layer) to ~ 60 nm (ultrathin charge tunneling layer) without sacrificing the thermal stability of the C-MAPbI 3 film. The vanadium oxide (VO x ) sol was spin-coated on the ~ 60 nm PMMA-encapsulated C-MAPbI 3 film and annealed at 150 °C for 20 min to act as a hole transport layer (HTL). The VO x sol could be annealed without causing thermal degradation to the C-MAPbI 3 film. With this discovery, the VO x may replace the thermally unstable organic HTLs in n–i–p PSCs. This low-cost and facile metal oxide sol route would lead to economic and scalable production of all-metal oxide CTL-based PSCs with significantly improved device operational stability.

materials science, multidisciplinary