Abstract:To improve the microstructure of low-temperature-processed CsPbIBr2 films, a chlorobenzene (CB) and isopropyl alcohol (IPA) mixed solution is used as an antisolvent to fabricate CsPbIBr2 films. It is found that the modified film by the mixed antisolvent demonstrates a better morphology, crystallinity, absorption of sunlight, less trap-state density (Ntrap), and suppressed carrier recombination. The modified perovskite solar cells (PSCs) without a hole-transport layer (HTL) achieve a champion efficiency of 7.05%, being much higher by 28.18% than that of the Reference-PSCs without an antisolvent. Moreover, the HTL of undoped zinc phthalocyanine (ZnPc) prepared by solution processing is used to promote charge transfer and protect the CsPbIBr2 film from damage caused by humid air at the CsPbIBr2/carbon interface. The best PSC with a structure of FTO/TiO2/CsPbIBr2/ZnPc/carbon yields a champion efficiency of 8.48% (Reference-PSC, 5.50%) with an open-circuit voltage of 1.23 V. The modified PSCs without encapsulation demonstrate improved humidity stability and retain about 90% (Reference-PSC, ∼70%) of their initial efficiency after storage at a 20% relative humidity in air for 30 days. In addition, the modified PSCs possess good light and thermal stability. Our work provides a feasible low-temperature (150 °C) process to prepare CsPbIBr2 films with the preferred orientation and stable, efficient all-inorganic PSCs (200 °C).The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.1c03554.Photovoltaic parameters, PCE, and J–V curves of the devices treated with the CI antisolvent with different IPA:CB volume ratios; photovoltaic parameters, PCE, and J–V curves of CI-ZnPc-PSCs with different ZnPc concentrations; summary of low-temperature-processed carbon-based all-inorganic CsPbIBr2 PSCs reported in recent years; photographs of color evolution of the Reference-, CI-, IPA-, and CB-films treated at 30 °C for 600 s; thickness of the Reference-film and the CI-film measured by an ellipsometer (PDF)This article has not yet been cited by other publications.

Efficient Stabilization and Passivation for Low-Temperature-Processed Γ-Cspbi3 Solar Cells

Efficient Stabilization and Passivation for Low-Temperature-Processed γ-CsPbI 3 Solar Cells

Stable Hole-Free, Carbon-Based CsPbI3 Perovskite Solar Cells Achieving 12.45 %-Efficiency at a Low Temperature with Mn Doping and Excess CsBr Simultaneously

Low-temperature Preparation Achieving 10.95%-Efficiency of Hole-Free and Carbon-Based All-Inorganic CsPbI3 Perovskite Solar Cells

A Stabilized Γ-Cspbi3 by Poly(allylamine Hydrochloride) for Wide-Band Gap Perovskites Solar Cells with Enhanced Performance

Bifunctional Passivation for Efficient and Stable Low-Temperature Processed All-Inorganic CsPbIBr2 Perovskite Solar Cells

Towards low-temperature processing of efficient $γ$-CsPbI$_3$ perovskite solar cells

Temperature-Reliable Low-Dimensional Perovskites Passivated Black-Phase CsPbI3 toward Stable and Efficient Photovoltaics

A Mixed Antisolvent-Assisted Crystallization Strategy for Efficient All-Inorganic CsPbIBr2 Perovskite Solar Cells by a Low-Temperature Process

Low temperature-processed stable and high-efficiency carbon-based CsPbI2Br perovskite solar cells by additive strategy

Improving Crystallization and Stability of Perovskite Solar Cells Using a Low-Temperature Treated A-Site Cation Solution in the Sequential Deposition

Fabrication of high‐quality CsPbI3 perovskite films via phosphorus pentachloride additive

Interface Engineering of Low Temperature Processed All-Inorganic CsPbI2Br Perovskite Solar Cells Toward PCE Exceeding 14%

Clothe CsPbI3 perovskite in robust phase-pure armor to boost the thermal stability

An efficient post-treatment strategy with acetylacetone for low temperature CsPbI2Br solar cells

Stabilizing the Α-Phase of CsPbI3 Perovskite by Sulfobetaine Zwitterions in One-Step Spin-Coating Films

Enhancement of thermal stability for perovskite solar cells through cesium doping

Optimizing the Substrate Pre-Heating and Post-Annealing Temperatures for Fabricating High-Performance Carbon-Based CsPbIBr2 Inorganic Perovskite Solar Cells

Phthalimide Additive-Promoted Ambient Fabrication of Inorganic CsPbI2Br Perovskite for Highly Efficient and Stable Solar Cells

A Mixed Antisolvent-Assisted Crystallization Strategy for Efficient All-Inorganic CsPbIBr 2 Perovskite Solar Cells by a Low-Temperature Process

Low‐Temperature Crystallization of CsPbIBr 2 Perovskite for High Performance Solar Cells