Friction and Wear Mechanisms of 316L Stainless Steel in Dry Sliding Contact: Effect of Abrasive Particle Size

A. Jourani,S. Bouvier

DOI: https://doi.org/10.1080/10402004.2014.955229

IF: 2.056

2014-10-31

Tribology Transactions

Abstract:The present work investigates the dry sliding friction and wear behavior of 316L austenitic stainless steel. Wear tests are performed on a pin-on-plane configuration against abrasive silicon carbide grains ranging from very large (200 μm) to small (15 μm) particles. The experiments are conducted at room temperature under different normal loads of 25–75 N. The wear damage mechanisms and wear debris are analysed using scanning electron microscope (SEM) observations. It is shown that for small abrasive particles, the friction coefficients increase with increasing normal load. However, for large abrasive particles, a reverse trend is observed. This difference is partly explained by a change in wear mechanisms. Finally, surface roughness measurment of the worn surfaces are performed after wear tests. The relationship between the 3D fractal dimension and wear rate is investigated based on fractal theory. The 3D fractal analysis of the worn surfaces showed that higher values of fractal dimensions indicate a larger real contact area and therefore a better wear resistance of the 316L stainless steel.

engineering, mechanical

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to explore the friction and wear behavior of 316L austenitic stainless steel in dry sliding contact, especially the influence of abrasive particles of different particle sizes (such as silicon carbide) on the friction coefficient and wear mechanism. Specifically:

- **Research Background**: 316L stainless steel is widely used in many industrial fields because of its excellent mechanical properties and antioxidant properties, but it performs poorly in terms of friction and wear characteristics. Therefore, it is of great significance to understand how abrasive particles of different particle sizes affect the friction and wear mechanism of this material.

- **Research Purposes**:
- To explore the influence of abrasive particles of different particle sizes (from 15 micrometers to 200 micrometers) on the friction coefficient and wear rate of 316L stainless steel in dry sliding contact.
- To analyze the changing trend of the friction coefficient under different load conditions (from 25 N to 75 N).
- To observe the worn surface by scanning electron microscope (SEM) and identify different microscopic wear mechanisms.
- To study the roughness of the worn surface by using the 3D fractal analysis method and explore the relationship between the fractal dimension and the wear rate.

- **Core Issues**: The paper aims to reveal how the size of abrasive particles changes the friction and wear mechanisms and the physical mechanisms behind these changes. For example, small particles cause the friction coefficient to increase with the increase of load, while large particles show the opposite trend. In addition, the paper also explores the fractal characteristics of the worn surface and its relationship with the wear rate.

Through the above research, the author hopes to provide theoretical basis and technical support for optimizing the wear - resistant performance of 316L stainless steel in practical applications.