Abstract:Austenitic steels are commonly used in aero-engine components owing to their higher thermal resistance to wear and corrosion. This study investigates the high-temperature dry sliding wear behaviour of direct metal laser-sintered (DMLS) austenitic stainless steel (S.S 316L) up to 400°C . A dry sliding reciprocating wear test conducted on a high-frequency tribometer with a ball-on-flat setup. High-hardness chrome steel (900 HV 0.5 ) and alumina (1165 HV 0.5 ) balls of 6 mm diameter were used as the steel and ceramic counterbodies against 316L specimen (320 ± 5 HV 0.5 ). When tested against the chrome steel, the initial average coefficient of friction (CoF) decreased to a lower value (0.45) during the initial running-in period. However, with rising temperatures, the CoF also increased, stabilizing at 0.6 under steady-state conditions. A similar CoF pattern was observed in experiments with the alumina counterbody. Wear resistance declined at 100°C , followed by an increase at 200°C due to the development of an oxide glaze on the surface. Subsequently, wear resistance decreased as the temperature continued to rise. Up to 200°C , the wear mechanism was characterised by a combination of abrasive and oxide debris wear, transitioning to adhesive wear with plastic deformation at higher temperatures ( 400°C ). Diffraction (XRD) analysis revealed the formation of oxide layers and martensite phase at higher temperatures, contributing to the observed improved wear resistance around 200°C . However, these oxide layers were progressively removed from the surface at 400°C , leading to an increased wear. The measured wear rates are two times lower, up to 200°C , compared to the reported values for conventional 316L due to the fine microstructure and higher hardness of DMLS SS 316L. This results in potentially rendering it suitable for applications where high-temperature (up to 200°C ) wear-resistant S.S is needed. This study provides further insights into the importance of post-treatment of DMLS parts for temperature beyond 400°C ).

High-temperature dry sliding wear behavior of additively manufactured austenitic stainless steel (316L)

Experimental Investigation into the Dry Reciprocating Wear Behavior of Additively Manufactured Austenitic Stainless Steel (316L) Alloys

Differentiation of specific wear rates of AISI 304 austenitic and AISI 2205 duplex stainless steels at room and high temperatures

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

Tribological behavior investigation of 316L stainless steel samples processed by selective laser melting

Thermal stability and microstructural evolution of additively manufactured 316L stainless steel by laser powder bed fusion at 500–800 °C

High-Temperature Mechanical Properties of Additively Manufactured 420 Stainless Steel

Investigation into Friction and Wear Characteristics of 316L Stainless-Steel Wire at High Temperature

Influence of heat treatment temperature on the microstructural, mechanical, and wear behavior of 316L stainless steel fabricated by laser powder bed additive manufacturing

High-Temperature Tribology of Selective Laser-Melted Titanium Alloys: Role of Adhesive Wear

An Experimental Investigation into the Dry Reciprocating Wear Behavior of Additively Manufactured AlSi10Mg Alloys

Long-Term Effects of Temperature Exposure on SLM 304L Stainless Steel

Additively manufactured 316L stainless steel via laser powder directed energy deposition (LP-DED): Mechanical properties at cryogenic and elevated temperatures

Effect of 316L Stainless Steel Fabrication on Oxidation Resistance, Surface Morphology, and Hot Tensile Behavior

Effect of nitrogen on high temperature dry sliding wear of 316L (N) stainless steel

Tribological performance of 410L martensitic stainless steel parts manufactured by Laser directed energy deposition

Investigations on tribological behavior under lubricated condition of post heat treated additively manufactured SS316L parts

Comparison of high-temperature friction and wear behaviours of Ti6Al4V produced by additive manufacturing and casting

Enhanced Corrosion Resistance of Additively Manufactured 316L Stainless Steel after Heat Treatment

Studies of high temperature sliding wear of medium carbon Nickel-Chromium based alloy steel

High Temperature Wear Behavior of AlMgScZr Alloy Produced By Laser Powder Bed Fusion