Abstract:A new type of non-oxide sintering additive of YH2 was introduced for the fabrication of AlN ceramics with high thermal conductivity and flexural strength. The effects of YH2 addition (0–5 wt%) on the phase composition, densification, microstructure, thermal conductivity and flexural strength of pressureless sintered AlN ceramics were investigated and compared with those Y2O3-added samples (1–5 wt%). The addition of 1 wt% YH2 led to an in-situ reduction reaction with oxygen impurities, the formation of Y2O3 and finally the formation of yttrium aluminate, which in turn improved densification and microstructure. A high flexural strength (408.69 ± 28.23 MPa) was achieved. The addition of 3 wt% YH2 increased the average grain size and purified the lattice. All these effects are believed to help achieve a high thermal conductivity of 184.82 ± 1.75 W·m−1·K−1. Although the thermal conductivity was close to the value of 3 wt% Y2O3-added sample, its strength was much increased to 381.53 ± 43.41 MPa. Meanwhile, it demonstrated a good combination of the thermal conductivity and flexural strength than the values reported in some literature. However, further increasing the YH2 addition to 5 wt% resulted in a high N/O ratio that inhibited the densification behavior of AlN ceramics. The current study showed that AlN ceramics with excellent thermal and mechanical properties could be obtained by the introduction of a suitable YH2 additive.

New Insight on the Effect of Yttria-Based Secondary Phases on Sintering and Electrical Behavior of Aluminum Nitride Ceramics

Effects of binary additives B2O3–Y2O3 on the microstructure and thermal conductivity of aluminum nitride ceramics

Effects of Y2O3 and Yttrium Aluminates As Sintering Additives on the Thermal Conductivity of AlN Ceramic Substrates

Phase Composition, Crystal Structure and Microwave Dielectric Properties of Nb-Doped Yttrium Aluminum Garnet Ceramics

Phase composition, microstructure, electrical and thermal properties of TiN and Yb2O3-Sm2O3 doped AlN ceramics

Comparative Study on Electrical Conductivity of CeO2-Doped AlN Ceramics Sintered by Hot-Pressing and Spark Plasma Sintering

Effect of Y2O3 on low temperature sintering and thermal conductivity of AlN ceramics

Microstructure and thermal conductivity of AlN ceramics with ultra-fine Y2O3 powder addition

Effect of YF3 on densification behavior and thermal conductivity of AlN ceramics with Y2O3–YF3 additives under reducing atmosphere

Fabrication and thermal conductivity of AlN/BN ceramics by spark plasma sintering

Phase composition, crystal structure, and microwave dielectric properties of Nb-doped and Y-deficient yttrium aluminum garnet ceramics

Effects of YH2 addition on pressureless sintered AlN ceramics

Microstructure and thermal conductivity of aluminium nitride with (CaY)F3 as the sintering aid

Influence of the sintering methods on the electrical properties of cerium-doped aluminium nitride ceramics

Microstructure and thermal conductivity of aluminium nitride with (YCa)F3 as sintering aid

Effect of Sintering Temperature and Yttrium Composition on the Densification, Microstructure and Mechanical Properties of Spark Plasma Sintered Silicon Nitride Ceramics with Al2O3 and Y2O3 Additives

RESEARCH ON THE REACTION SYNTHESIS OF AlN-BASED CERAMICS WITH THE ADDITION OF Y2O3

In-situ synthesis of Yttria-based precipitates and their effects on Fe12Cr6Al in laser powder bed fusion

Characterization of the Microstructure of Sintered Aln by Sem and Tem

The quantitative investigation of the lattice oxygen and grain edge oxygen on the thermal conductivity of aluminum nitride ceramics

Secondary crystalline phases and mechanical properties of heat-treated Si3N4