Abstract:The content of Zn and Mg directly influences the microstructure characteristics of Al–Zn–Mg–Cu alloys. In the present study, the solidification phases of three as-cast Al–Zn–Mg–Cu alloys with different Zn/Mg ratio (1.5, 1.8 and 2.1 at.%, successively) were thoroughly investigated, and their evolutions during homogenizations were analyzed with the aid of optical microscopy (OM), scanning electron microscopy (SEM), differential scanning calorimetry (DSC), and X-ray diffraction (XRD). The results showed that serious dendritic segregation existed in the as-cast microstructures. In the as-cast alloys with three different Zn/Mg ratio, the secondary phases are represented by non-equilibrium intermetallic phases (Mg(Zn,Cu,Al) 2 and Al 2 Cu) and precipitate MgZn 2 phase. Thereinto, the Mg(Zn,Cu,Al) 2 phase possessed a majority, which was determined through computational analysis of solidification processes. With the increase of Zn/Mg ratio, the amount of Mg(Zn,Cu,Al) 2 phase continuously decreased, while the content of Al 2 Cu phase showed only minor variation. As the Zn/Mg ratio increased, the strength and hardness of the as-cast alloy gradually improved. The Zn/Mg ratio has a significant impact on the dissolution and transformation of the secondary phases during homogenization process. As the Zn/Mg ratio increased, the melting point of the as-cast eutectic gradually decreased. Additionally, due to the higher diffusion rate of Zn compared to Mg and Cu elements, the dissolution rate of the secondary phase increased accordingly. At relatively low temperatures (380, 410, and 440 °C), phase transformation from the Mg(Zn,Cu,Al) 2 phase to the Al 2 CuMg phase occurred in all three alloys. However, phase transformation was only present in Low/Mid-Zn/Mg ratio alloys at 470 °C. These differences are attributed to the varying diffusion rates of Zn, Mg, and Cu elements during the homogenization process. The implementation of a two-stage homogenization process effectively addresses the issue of residual Al 2 CuMg phase in Low/Mid-Zn/Mg ratio alloys.

Solid-Solution Incipient Melting of Homogenized Al–Cu–Mg–Fe Alloy

Solidification Paths and Phase Components at High Temperatures of High-Zn Al-Zn-Mg-Cu Alloys with Different Mg and Cu Contents

Tailoring intermetallic phase and mechanical property improvement in a novel Al-Zn-Mg-Cu-Y alloy via homogenization treatment

The evolution mechanism of the second phase during homogenization of Al-Zn-Mg-Cu aluminum alloy

High-Temperature Phase Transformations in Al-Li-Cu-Mg-Zr-Sc Alloy Studied via In Situ Electron Microscopy

Microstructural Characterization of the As-Cast and Homogenized Al-Cu-Mg-Ag Alloy

The strengthening role of micro-sized phases and nano-precipitates in Al–Mg 2 Si–Cu(–Ni) alloys at 25 °C and 350 °C

Melting, Solidification, and Viscosity Properties of Multicomponent Fe-Cu-Nb-Mo-Si-B Alloys with Low Aluminum Addition

Formation of intermetallic phases during solidification in Al-Mg-Mn 5xxx alloys with various Mg levels

Microstructure Evolution and Homogenization Kinetics of 15Cr–30Ni–Fe Heat‐Resistant Alloy

Effect of Zn/Mg ratio on the microstructure and mechanical properties of as-cast Al–Zn–Mg–Cu alloys and the phase transformation during homogenization

Effect of ultrasonic melt processing and cooling rate on microstructure evolution of Al–Cu–Mn–Mg–Fe–Si alloy

Fe microalloying during the in-situ synthesis of homogeneous CuCrFe alloys by aluminothermic Self-propagating

Research on homogeneous nucleation and microstructure evolution of aluminium alloy melt

Research on Homogenization Treatment of Mg-8wt.% Sn-1.5 Wt.% Al Alloy

Highly stable coherent nanoprecipitates via diffusion-dominated solute uptake and interstitial ordering

In Situ Observation of Microstructure and Precipitate Phase Transformation during the Solidification of Mg‐Containing GH3625 Alloy at Different Cooling Rates

Alloying effect of Mg on microstructure and mechanical properties at 300 °C of Al–5Cu–1Mn–0.5Ni heat-resistant alloy

Effect of Composition on Microstructural Evolution during Homogenization of 7XXX Alloys

Decomposition of Supersaturated Solid Solution in Fast-Quenched Al-Co-Zr and Al-Fe-Co-Zr Alloys

Effects of electromagnetic stirring and subsequent homogenization treatment on the microstructure and mechanical properties of Al70Zn10Mg10Cu5Si5 multi-component alloy