Abstract:The content of Zn and Mg directly influences the microstructure characteristics of Al–Zn–Mg–Cu alloys. In the present study, the solidification phases of three as-cast Al–Zn–Mg–Cu alloys with different Zn/Mg ratio (1.5, 1.8 and 2.1 at.%, successively) were thoroughly investigated, and their evolutions during homogenizations were analyzed with the aid of optical microscopy (OM), scanning electron microscopy (SEM), differential scanning calorimetry (DSC), and X-ray diffraction (XRD). The results showed that serious dendritic segregation existed in the as-cast microstructures. In the as-cast alloys with three different Zn/Mg ratio, the secondary phases are represented by non-equilibrium intermetallic phases (Mg(Zn,Cu,Al) 2 and Al 2 Cu) and precipitate MgZn 2 phase. Thereinto, the Mg(Zn,Cu,Al) 2 phase possessed a majority, which was determined through computational analysis of solidification processes. With the increase of Zn/Mg ratio, the amount of Mg(Zn,Cu,Al) 2 phase continuously decreased, while the content of Al 2 Cu phase showed only minor variation. As the Zn/Mg ratio increased, the strength and hardness of the as-cast alloy gradually improved. The Zn/Mg ratio has a significant impact on the dissolution and transformation of the secondary phases during homogenization process. As the Zn/Mg ratio increased, the melting point of the as-cast eutectic gradually decreased. Additionally, due to the higher diffusion rate of Zn compared to Mg and Cu elements, the dissolution rate of the secondary phase increased accordingly. At relatively low temperatures (380, 410, and 440 °C), phase transformation from the Mg(Zn,Cu,Al) 2 phase to the Al 2 CuMg phase occurred in all three alloys. However, phase transformation was only present in Low/Mid-Zn/Mg ratio alloys at 470 °C. These differences are attributed to the varying diffusion rates of Zn, Mg, and Cu elements during the homogenization process. The implementation of a two-stage homogenization process effectively addresses the issue of residual Al 2 CuMg phase in Low/Mid-Zn/Mg ratio alloys.

The evolution mechanism of the second phase during homogenization of Al-Zn-Mg-Cu aluminum alloy

Effect of Zn/Mg ratio on the microstructure and mechanical properties of as-cast Al–Zn–Mg–Cu alloys and the phase transformation during homogenization

Tailoring intermetallic phase and mechanical property improvement in a novel Al-Zn-Mg-Cu-Y alloy via homogenization treatment

Effects of homogenization on the microstructural evolution of a novel Zr and Er containing Al–Mg–Zn alloy

Solidification Paths and Phase Components at High Temperatures of High-Zn Al-Zn-Mg-Cu Alloys with Different Mg and Cu Contents

Mechanical and Thermodynamic Behaviors of the Second Phases in Al–Zn–Mg–Cu Alloys

Investigation of Microstructures in As-Cast and Homogenized Al-7.8Zn-1.6Mg-1.8Cu Aluminum Alloy

Phase transformation from phase to S phase at grain boundary during annealing in rapidly-solidified Al-Zn-Mg-Cu alloy

DISSOLUTION OF THE SECOND PHASE DURING CONTINUOUS HEATING PROCESS

Phase transformation from η phase to S phase at grain boundary during annealing in rapidly-solidified Al-Zn-Mg-Cu alloy

Solid-Solution Incipient Melting of Homogenized Al–Cu–Mg–Fe Alloy

Microstructural Evolution During Homogenization of DC Cast 7085 Aluminum Alloy

Evolution of micropores and second phases during hot deformation of 2050 Al-Li alloy

Three-Stage Homogenization of Al-Zn-Mg-Cu Alloys Containing Trace Zr

Microstructural Evolution of 2026 Aluminum Alloy During Homogenization

Microstructural Characterization of the As-Cast and Homogenized Al-Cu-Mg-Ag Alloy

Evolution of the Second-Phase Particles and Their Effect on Tensile Fracture Behavior of 2219 Al-xCu Alloys

Homogenization heat treatment of 2099 Al–Li alloy

Synergistic effect of gradient Zn content and multiscale particles on the mechanical properties of Al–Zn–Mg–Cu alloys with coupling distribution of coarse–fine grains

Microstructural Evolution and Kinetics of 7075 Al Alloy During Homogenization Treatment

High-Temperature Phase Transformations in Al-Li-Cu-Mg-Zr-Sc Alloy Studied via In Situ Electron Microscopy