Abstract:The research was mainly focused on the phase transformation of Ti-42Al-5Mn (at%) alloy produced by vacuum induction melting (VIM) and vacuum arc remelting (VAR) followed by wrought process. The phase transformation kinetics of the alloy during continuous cooling under the cooling rates of 0.1 degrees C/s, 0.5 degrees C/s, 2 degrees C/s, 10 degrees C/ s, 50 degrees C/s, and 200 degrees C/s were identified by the Gleeble-3800 system, which is finally used to construct a schematic continuous cooling transformation (CCT) diagram of this alloy. The related phase composition, microstructure and property of the alloy were studied using X-ray diffraction (XRD), electron probe micro analyzer (EPMA), transmission electron microscope (TEM) and Vickers hardness (HV). It shows that six kinds of phase transformation are existed during continuous cooling from 1300 degrees C with the cooling rates of 0.1 degrees C/s, 0.5 degrees C/s, 2 degrees C/s, 10 degrees C/s, 50 degrees C/s, 200 degrees C/s and WQ, including beta ->alpha(2)', beta ->alpha, beta ->gamma, beta ->beta(o)/alpha ->alpha(2), alpha(2)->alpha(2)/gamma and alpha(2)/gamma ->beta(o,sec).It reveals that partial transformations would be inhibited when the cooling rate is relatively high. The martensitic structures (alpha(2)') obtained by beta ->alpha(2) were formed under the WQ condition after holding at 1300 degrees C for 5min, and it will be completely restrained below the cooling rate of WQ. For the beta ->gamma, it is restrained if the cooling rates are higher than 50 degrees C/s. The alpha(2)->alpha(2)/gamma could be also suppressed when cooling with 200 degrees C/s, and the gamma lath within the supersaturated alpha(2)-grains would be formed at lower cooling rate below 50 degrees C/s. For 0.5 degrees C/s and 0.1 degrees C/s, a small amount of dotted beta(o) (beta(o,sec)) phases can be formed in the lamellar interfaces, which is proved the reaction products of alpha(2)/gamma ->beta(o,sec). Furthermore, the effect of cooling rates on the microstructure, including interlamellar spacing (lambda) and gamma grains are also identified and discussed.

DISSOLUTION OF THE SECOND PHASE DURING CONTINUOUS HEATING PROCESS

Phase Field Simulation for Non-Isothermal Solidification of Multicomponent Alloys Coupled with Thermodynamics Database

Dissolution kinetics of irregular second phase in as-cast Cu-Ti alloys via a multi-particle dissolution model

Multi-component Phase-Field Simulation of Microstructural Evolution and Elemental Distribution in Fe–Cu–Mn–Ni–Al Alloy

The evolution mechanism of the second phase during homogenization of Al-Zn-Mg-Cu aluminum alloy

Phase-Field Simulation of Non-Isothermal Dendritic Growth of Binary Alloy

Simulation of Isothermal Solidification of Multi-Component Alloys with Phase-Field Method

Comparative Analysis of Isothermal and Non-Isothermal Solidification of Binary Alloys Using Phase-Field Model

Phase-field Simulation of Effect of Phase-field Parameters on Solidification Process of Multicomponent Alloys

Observations and simulations for phase separation process of immiscible Fe50Sn50 alloy droplets placed on a chilling surface

Phase-field simulation of re-dissolution of γ′ phase in Ni–Al alloy by continuous and second-order aging treatment

Modeling the Overall Solidification Kinetics for Undercooled Single-Phase Solid-Solution Alloys. II. Model Application

Phases Formation and Evolution at Elevated Temperatures of Al–12Si–3.8Cu–2Ni–1Mg Alloy†

Secondary Phase Precipitation in Fe-22Mn-9Al-0.6C Low-Density Steel during Continuous Cooling Process

Phase-field Simulation of Solidification in Multicomponent Alloys Coupled with Thermodynamic and Diffusion Mobility Databases

Simulation of Nucleation and Coalescence of Second Phase Droplets During Earth-Based Solidification Process of Immiscible Alloys

Cooling Rate Effects on Microstructure and Diffusion Behaviour in Ti65 Alloy: Insights from a Modified Diffusion Model

Quantitative Phase-Field Modeling of Rapid Alloy Solidification

Influence of heat treatment on morphology and quantity of eutectic phases of Al alloys with different cooling rates

Phase Transformation Behavior of a Mn Containing Β-Solidifying Γ-Tial Alloy During Continuous Cooling

Resummation in Hot Field Theories