Total Subgap Range Density of States-Based Analysis of the Effect of Oxygen Flow Rate on the Bias Stress Instabilities in a-IGZO TFTs
Ga Won Yang,Jingyu Park,Sungju Choi,Changwook Kim,Dong Myong Kim,Sung-Jin Choi,Jong-Ho Bae,Il Hwan Cho,Dae Hwan Kim
DOI: https://doi.org/10.1109/ted.2021.3130219
IF: 3.1
2022-01-01
IEEE Transactions on Electron Devices
Abstract:In this study, the oxygen flow rate (OFR) dependence of negative bias illumination stress (NBIS) and positive bias stress (PBS) in amorphous indium-gallium-zinc-oxide (a-IGZO) thin-film transistor (TFT) devices was investigated. Unlike in previous studies, our study simultaneously considered and analyzed the bias stress-induced degradation mechanisms by charge trapping and defect creation. NBIS and PBS instability were measured according to the OFR splits of bottom-gate (BG) IGZO TFTs and the behavior of full subgap range density of states (DOS) was experimentally tracked with especial emphasis on deep-level oxygen vacancy (${V}_{\text {O}}$ ) peak. It was found that the observed DOS variation was consistent with the ${V}_{\text {O}}$ ionization model during NBIS. In addition, the threshold voltage shift by charge trapping (${\Delta } {V}_{\text {T,CT}}$ ) and the threshold voltage shift by defect creation, i.e., change of DOS, (${\Delta } {V}_{\text {T,DOS}}$ ) were separated and extracted through the subthreshold slope decomposition method. After NBIS, the threshold voltage shift (${\Delta } {V}_{\text {T}}$ ) was composed of a component by charge trapping and a component with the ionization of ${V}_{\text {O}}$ . After PBS, ${\Delta } {V}_{\text {T}}$ was dominated by a component arising due to charge trapping. Fitting through the stretched exponential function (SEF) was performed for each separately extracted ${\Delta } {V}_{\text {T}}$ , and the activation energy for each ${\Delta } {V}_{\text {T}}$ was extracted using the inverse Laplace transform method through the extracted ${\Delta } {V}_{\text {T0}}$ , $\tau $ , and $\beta $ . Activation energy by charge trapping and DOS was extracted from NBIS and PBS, respectively. As a result of simultaneously considering the two degradation mechanisms, the extracted activation energy was located between the previous values. Experimentally extracted sets of DOS-specific parameters before and after bias stress were applied to technology computer-aided design (TCAD) simulations. Accurate reproduction of TFT current–voltage (${I}$ –${V}$ ) curves before and after bias stress and recovery suggests that the methodology and parameter set used in this study are reasonable and potentially useful for a more robust and systematic analysis of the bias stress-induced instability in a-IGZO BG TFTs.
engineering, electrical & electronic,physics, applied