Abstract:The corrosion resistance to molten iron of four kinds of carbon bricks used in blast furnace hearth were investigated to elaborate the corrosion mechanism through the macroscopic and microscopic analysis of carbon bricks before and after reaction and thermodynamic analysis. The macroscopic analysis showed that brick A had the lowest degree of corrosion and highest uniformity at different heights, attributing to its moderate carbon content of 76.15%, main phases of C, Al2O3, SiC, and Al6Si2O13 (mullite), and lower resistance to molten iron infiltration, etc. The microscopic analysis showed that all the carbon bricks had more and larger pores than the original carbon bricks. The phenomena of the iron beads adhering to carbon brick and iron infiltration were observed between the interface of carbon brick and molten iron. In addition, the obvious corrosion process was presented that the carbon matrix was broken and peeled off during the iron infiltration process. For the carbon brick being corroded, the dissolution of carbon was the predominant reaction. The higher the carbon solubility of the molten iron, the easier the corrosion on the carbon brick. Al2O3 and SiC enhanced the corrosion resistance to molten iron of carbon bricks, and SiO2 could react with carbon to form pores as channels for the penetration of molten iron and increase the corrosion on carbon bricks. A higher graphitization degree of carbon bricks was beneficial to lessen their corrosion degree. The corrosion on carbon bricks by molten iron could be attributed to three aspects: carburization, infiltration, and scouring of molten iron. The carburization process of molten iron was the main reaction process. The molten iron infiltration into the carbon bricks facilitated the dissolution of carbon and destroyed the structure and accelerated the corrosion of the carbon bricks. The scouring of molten iron subjected the iron–carbon interface to interaction forces, promoting the separation of the exfoliated fragmented carbon brick from the iron–carbon interface to facilitate a new round of corrosion process.

Composition and microstructure of a periclase–composite spinel brick used in the burning zone of a cement rotary kiln

Corrosion mechanism of cement-bonded Al2O3–MgAl2O4 pre-cast castables in contact with molten steel and slag

Degradation mechanism of high alumina refractory bricks by reaction with deposits in a rotary kiln for fluxed iron ore pellets production

Mechanism of in-situ formation of spinel and its effect on the mechanical properties of Al2O3–C refractories

Effects of Aluminium Oxide Content on the Regenerated Magnesia-Calcium Bricks for Cement Rotary Kiln

Corrosion in high alumina refractory serviced in a bench-scale entrained flow gasifier

Corrosion behavior of CaO–Al2O3–SiO2–MgO-Cr2O3 slag on MgO refractory brick for smelting of chromite

Microstructure evolution, mechanical characteristics and erosion behavior of Cr2O3–Al2O3–MgO–ZrO2 refractories in molten reduction slag

Effects of different particle size of spinel and Y2O3 additive of the periclase-spinel refractory on the sintering densification and corrosion resistance to copper smelting slag

Degradation behaviors of cement-free corundum-spinel castables in Ruhrstahl Heraeus refining ladle: Role of infiltrated steel

Effect of Calcium Aluminate-Based Additive on Properties of Periclase-Carbon Refractories for Steel-Teeming Ladles

Formation mechanism of the brittle layer in carbon brick of blast furnace hearth

Corrosion of high-chrome refractory materials by high-sodium slag in an entrained-flow gasifier

Dissolution of Al2O3–C bricks in 45 wt% CaO-45 wt% SiO2-x wt% CaF2-(10-x) wt% Na2O slag

Mullite–zirconia composite for the bonding phase of refractory bricks in hazardous waste incineration rotary kiln

Thermodynamic calculation and microstructure characterization of spinel formation in MgO–Al2O3–C refractories

Corrosion of MgO–C Refractory with Ladle Slags

Comparative Analysis on the Corrosion Resistance to Molten Iron of Four Kinds of Carbon Bricks Used in Blast Furnace Hearth

Interactions of Cr2O3–Al2O3–ZrO2 refractory with slags in an entrained-flow coal-water slurry gasifier

Influence of bonding systems on the properties of Al 2 O 3 -MgO refractory castables: Aluminate cement and alumina silica gel

Interactions of high-chromia refractory materials with infiltrating coal slag in the oxidizing atmosphere of a cyclone furnace