TF-Al/TiC highly reactive composite particle for application potential in solid propellants
Deqi Wang,Xinfu Cao,Jie Liu,Zhimiao Zhang,Xiaoxun Jin,Jianbing Gao,Haomiao Yu,Sensen Sun,Fengsheng Li
DOI: https://doi.org/10.1016/j.cej.2021.130674
IF: 15.1
2021-12-01
Chemical Engineering Journal
Abstract:<p>Aluminum (Al) powder is widely used in solid propellants to improve specific impulse. But the dense alumina (Al<sub>2</sub>O<sub>3</sub>) on the surface of Al will reduce reactivity and heat release of Al. The phenomenon that Al<sub>2</sub>O<sub>3</sub> and titanium carbide (TiC) react to generate gas and form pores has been found. Combined this phenomenon, thick flake Al/TiC (TF-Al/TiC) highly reactive composite particle was designed, which has the structure of TiC embedded in the TF-Al. Then TF-Al/3%TiC, TF-Al/4%TiC, TF-Al/5%TiC and TF-Al/6%TiC were successfully prepared by two-step ball milling. Samples were characterized by SEM and TG-DSC. The results indicated that TF-Al/TiC highly reactive composite particle was a finely dispersed powder sample and their DSC curves had exothermic peak before 1000 ℃. And when the TiC content was less than 5%, as the content of TiC added increases, the heat release increased. And TF-Al/5%TiC had the highest heat release (21419 J/g). Furthermore, the reaction process of TF-Al/5%TiC was studied by SEM, EDS, XRD, XPS and TG-MS. Characterization results shown that Al<sub>2</sub>O<sub>3</sub> on the surface of TF-Al was decomposed by TiC in situ before 633 ℃, and the pores generated by the gaseous products would further increase the contact area between inside active Al and oxidant. So the reactivity and heat release of TF-Al/5%TiC had been improved. Those results indicated that TF-Al/TiC highly reactive composite particle has a promising application in solid propellants.</p>
engineering, chemical, environmental