Abstract:Two compositions Ce0.50Zr0.39La0.04Y0.07O2−δ and Ce0.25Zr0.65La0.04Y0.06O2−δ based on ceria-zirconia solid solutions were prepared as nanopowders using a continuous hydrothermal flow synthesis reactor, followed by either freeze-drying or hotplate-drying of the slurry. Each dried nanopowder was then subjected to 10h heat-treatment at 1000°C, 1100°C or 1200°C in air (to simulate accelerated ageing). The reducibility and hydrogen consumption of the oxidised samples were measured using temperature programmed reduction (TPR) up to 1000°C. The effects of composition, drying method and heat-treatment temperature were evaluated on the TPR profiles of the materials. The powders were further investigated using a range of analytical methods including UV/Vis spectroscopy (which yielded colour data), Raman spectroscopy, powder X-ray diffraction, BET surface area measurements and X-ray photoelectron spectroscopy (XPS). Chemometric methods were used to investigate relationships between the spectroscopic and total oxygen storage capacity (OSC) data. Principal component analysis (PCA) was used to provide a simple interpretation of the effects of various synthesis and treatment parameters on Raman spectra. Principal component regression (PCR) was used to build regression models relating the Raman spectra and the temperature of hydrogen consumption peak at several set temperatures in the TPR. The total hydrogen consumption of the materials was generally high, while the drying and heat-treatment conditions appeared to have a significant effect on the final properties of the resulting powders, such as the surface area and total oxygen storage capacity.

Self-propagating high-temperature synthesis of refractory powder materials based on zirconium diboride obtained from boron-containing mineral raw materials of the Republic of Kazakhstan

Boron Carbide Composites produced by Self-Propagating High-Temperature Synthesis

Synthesis and Analysis of Boride Ceramic Powders

Zrb2/Al2o3 Composite Powders Prepared by Self-Propagating High-Temperature Synthesis

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Kinetics of the Synthesis of Aluminum Boride by the Self-Propagating High-Temperature Synthesis Method

Characterization of Boride Ceramic Powders Prepared by SHS

Optimization of Aluminum Boride Synthesis in the Self-Propagating High-Temperature Synthesis Mode to Create Waste-Free Technology

Synthesis of Ultra-Fine and High-Pure Zirconium Diboride Powders Using Solution-Based Processing

A New Approach for the Synthesis of Powder Zinc Oxide and Zinc Borates with Desired Properties

Progress in Preparation of ZrB2 Nanopowders Based on Traditional Solid-State Synthesis

Self‐Propagating High‐Temperature Synthesis of Zirconolite Using CuO and MoO3 as the Oxidants

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Production of Zirconium-Niobium Alloys for Nuclear Reactors Fuel Rods via SHS Process

Self-Propagating High-Temperature Synthesis of Composite Material Based on Stabilized Zirconium Oxide1

Self-propagating high-temperature synthesis of ZrO2 incorporated Gd2Ti2O7 pyrochlore

On the Production of W–Fe–B Ternary Compounds by Self-propagating High-Temperature Synthesis

Synthesis and Characterization of High-Purity, High-Entropy Diboride Ceramic Powders by a Liquid Phase Method

Carbothermal Reduction Synthesis Of Zirconium Diboride Powders Assisted By Microwave

Applicability Boron-Containing Materials Obtained by Self-Propagating High-Temperature Synthesis in Radiation Protection Technology

Self-Propagating High-Temperature Reductive Synthesis of TiB_2-Al_2O_3 Composite Powders