Abstract:Borides and silicide of tungsten as the refractory intermetallic compounds have high mechanical properties, relatively good thermal shock, and chemical stability. Also, they have less brittleness than ceramic compounds that can lead to its usage in various industrial applications. In this work, for the first time, an alumina-based composite (WB-WB 2 -WSi 2 -Al 2 O 3 ) was produced by combustion synthesis using aluminothermic reaction of a quaternary mixture (Al-Si-WO 3 -B 2 O 3 ) as starting materials. According to standards defined by Merzhanov, Munir, and Anselmi, the combustion synthesis process for the system of Al-Si-WO 3 -B 2 O 3 is the type of self-propagating high-temperature synthesis (SHS). The milled mixture was formed into cylindrical specimens after cold pressing and was heat-treated using an oxyacetylene flame as the initiator of self-propagating high-temperature synthesis in the air atmosphere. The ignition, the maximum combustion temperature, and the progress speed of the combustion front were measured using several thermocouples and data logger device. The phases formed in the synthesis samples were characterized by X-ray diffraction (XRD) and field emission scanning electron microscope (FE-SEM). The results showed that the combustion front had a temperature above 1800 °C with a speed of about 20 mm·sec −1 . Microstructural observations showed the blades of tungsten borides with a hexagonal structure and spheres of tungsten silicates in the matrix of alumina phase. The average of particle size of borides and silicide of tungsten varies in the range of 100 to 200 nm, indicating the formation of sub-micron composite due to the high speed of the combustion synthesis process.

Zrb2/Al2o3 Composite Powders Prepared by Self-Propagating High-Temperature Synthesis

PREPARATION AND CHARACTERIZATION OF ZrB2-Al2O3 COMPOSITE POWDER BY SELF-PROPAGATING HIGH-TEMPERATURE SYNTHESIS WITH REDUCTIVE PROCESS

PREPARATION AND INTERFACE ANALYSIS OF ZrB2/Al2O3 COMPOSITE POWDERS

Self-Propagating High-Temperature Reductive Synthesis of TiB_2-Al_2O_3 Composite Powders

Self-Propagating High-Temperature Reductive Synthesis of TiB 2 -Al 2 O 3 Composite Powders

Characterization of Boride Ceramic Powders Prepared by SHS

Combustion and formation behavior of hybrid ZrB 2 and ZrC particles in Al-Zr-B 4C system during self-propagation high temperature synthesis

Synthesis and Analysis of Boride Ceramic Powders

Mechanism of Self-Propagating High-Temperature Synthesis of AlB2–Al2O3 Composite Powders

Reaction Behavior and Formation Mechanism of ZrB2 and ZrC from the Ni-Zr-B4C System during Self-Propagating High-Temperature Synthesis

Reaction Synthesis Of Nano-Scale Zrc Particulates By Self-Propagating High-Temperature Synthesis From Al-Zr-C Powder Mixtures

Preparation and Microstructure of In-Situ (zrb2+al2o3+al3zr)p/a356 Composite Synthesized by Melt Direct Reaction

Reaction Synthesis of ZrAl3 Intermetallic Compound and Its Nucleation Behavior

Synthesis of ZrB2-SiC-ZrC Composite Powders with Core-Shell Structure Via Sol-Gel Molecular Modulation

Synthesis of Al2O3-WSi2-WB2-WB composite in Al-Si-WO3-B2O3 system by self-propagating high-temperature synthesis

Preparation and characterization of TiB2-Al2O3 composite powder by combustion synthesis process

Boron Carbide Composites produced by Self-Propagating High-Temperature Synthesis

In Situ Fabrication and Microstructure of Micro-Nano ZrB2p/Al Composites

Self-propagating high-temperature synthesis of refractory powder materials based on zirconium diboride obtained from boron-containing mineral raw materials of the Republic of Kazakhstan

ZrB2–SiC–G Composite Prepared by Spark Plasma Sintering of In‐Situ Synthesized ZrB2–SiC–C Composite Powders

Phase Formation and Thermodynamic Analysis of Self-propagating High-temperature Synthesis Al–Zr–N System Composites