Abstract:Borides and silicide of tungsten as the refractory intermetallic compounds have high mechanical properties, relatively good thermal shock, and chemical stability. Also, they have less brittleness than ceramic compounds that can lead to its usage in various industrial applications. In this work, for the first time, an alumina-based composite (WB-WB 2 -WSi 2 -Al 2 O 3 ) was produced by combustion synthesis using aluminothermic reaction of a quaternary mixture (Al-Si-WO 3 -B 2 O 3 ) as starting materials. According to standards defined by Merzhanov, Munir, and Anselmi, the combustion synthesis process for the system of Al-Si-WO 3 -B 2 O 3 is the type of self-propagating high-temperature synthesis (SHS). The milled mixture was formed into cylindrical specimens after cold pressing and was heat-treated using an oxyacetylene flame as the initiator of self-propagating high-temperature synthesis in the air atmosphere. The ignition, the maximum combustion temperature, and the progress speed of the combustion front were measured using several thermocouples and data logger device. The phases formed in the synthesis samples were characterized by X-ray diffraction (XRD) and field emission scanning electron microscope (FE-SEM). The results showed that the combustion front had a temperature above 1800 °C with a speed of about 20 mm·sec −1 . Microstructural observations showed the blades of tungsten borides with a hexagonal structure and spheres of tungsten silicates in the matrix of alumina phase. The average of particle size of borides and silicide of tungsten varies in the range of 100 to 200 nm, indicating the formation of sub-micron composite due to the high speed of the combustion synthesis process.

Mechanism of Self-Propagating High-Temperature Synthesis of AlB2–Al2O3 Composite Powders

Dissolution–precipitation–substitution Mechanism of Self-Propagating High-Temperature Synthesis of Β-Nial(cu)/α(cu,ni) Composite

Ultra-fast synthesis and thermodynamic analysis of MoAlB by self-propagating high temperature combustion synthesis

Zrb2/Al2o3 Composite Powders Prepared by Self-Propagating High-Temperature Synthesis

Self-Propagating High-Temperature Reductive Synthesis of TiB_2-Al_2O_3 Composite Powders

Self-propagating high-temperature synthesis of MoAlB boride ceramics based on MAB-phase

Synthesis of Al2O3-WSi2-WB2-WB composite in Al-Si-WO3-B2O3 system by self-propagating high-temperature synthesis

Self-Propagating High-Temperature Reductive Synthesis of TiB 2 -Al 2 O 3 Composite Powders

Formation of TiB2-MgAl2O4 Composites by SHS Metallurgy

Preparation and characterization of TiB2-Al2O3 composite powder by combustion synthesis process

Combustion and formation behavior of hybrid ZrB 2 and ZrC particles in Al-Zr-B 4C system during self-propagation high temperature synthesis

Reaction mechanism of self propagating high temperature synthesis BN by thermite reaction

Synthesis of Al{sub 2}o{sub 3}-Tic and Al{sub 2}o{sub 3}-Tib{sub 2} Composite Powders by Combustion Method

Dissolution–precipitation mechanism of self-propagating high-temperature synthesis of mononickel aluminide

Kinetics of the Synthesis of Aluminum Boride by the Self-Propagating High-Temperature Synthesis Method

Exploring the Combustion Mechanism of Single Micron-Sized Aluminum Particles with a Numerical Model

Boron Carbide Composites produced by Self-Propagating High-Temperature Synthesis

Mechanism and Kinetics Analysis of AlN Combustion Synthesis

Self-propagating high-temperature synthesis and reaction mechanism of super-fine particles of gamma-LiAlO2

Reaction Behavior and Formation Mechanism of ZrB2 and ZrC from the Ni-Zr-B4C System during Self-Propagating High-Temperature Synthesis

Self-propagating high-temperature synthesis in Ti-W-C system