On the Production of W–Fe–B Ternary Compounds by Self-propagating High-Temperature Synthesis

Ece Soylu,Faruk Kaya,Meltem Sezen,Feray Bakan,Gabriella Tranell,Bora Derin

DOI: https://doi.org/10.1007/s11663-022-02625-z

2022-09-09

Metallurgical Transactions B (Process Metallurgy)

Abstract:In this study, one-step production of W 2 FeB 2 and WFeB compounds from oxide raw materials was carried out through cost-effective and energy-efficient aluminothermic self-propagating high-temperature synthesis (SHS). Accordingly, the feasibility of SHS in the production of W 2 FeB 2 and WFeB compounds was discussed. In addition, the selected SHS products of W 2 FeB 2 were re-melted through arc melting to investigate the structure modification of W 2 FeB 2 phase at high temperature. Prior to experimental work, raw material amounts, adiabatic temperatures, and phase diagram were calculated by FactSageTM software. The phase, microstructure, and compositional analyses were performed by X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive X-ray spectroscopy (EDS), respectively. The formation of γ -Fe, FeB and orthorhombic W 2 FeB 2 phases was detected for the samples that were mainly composed of WFeB, while W 2 FeB 2 -rich samples contained α -WB. Moreover, XRD analysis results suggested the formation of a trace amount of ternary W 3 FeB 3 phase in the W 2 FeB 2 -rich samples. High-temperature structure modification of W 2 FeB 2 (tetragonal) with arc melting was also successfully conducted. Vickers hardness test results were found to be in the range of 1007 to 2157 HV and WFeB containing samples possessed lower hardness than W 2 FeB 2 -rich samples. The experimental results revealed that SHS could be an alternative and promising feasible synthesis route for the production of W 2 FeB 2 /WFeB ternary borides.