Abstract:Hot pressing was used to produce compact ceramic samples with the following composition (wt.%): 60 ZrB2 + 20 SiC + 20 (Al2O3 + 32 t-ZrO2). The tetragonal modification of zirconium oxide in the eutectic was stabilized by yttrium oxide. The porosity of the samples was 3–5%. The mechanical properties of the ceramics (hardness HV, fracture toughness KIc, tensile strength δf, compressive strength Y, grain-boundary strength S, and bending strength σ) were studied. Analysis of the microstructure and elemental composition of the phases revealed that a defect-free structure developed in the ZrB2-based composite through strong Van Der Waals adhesive interaction at the SiC–Al2O3 interface, which increased the fracture toughness to 9.4 MPa ∙ m1/2. In turn, this increased the grain strength from 0.64 GPa for the basic composite to 3.46 GPa for the ZrB2–SiC composite with an oxide addition. An addition of Al2O3 + 32 wt.% t-ZrO2 was introduced in sufficient quantities not only to reduce the fracture stress but also to promote plastic deformation of the material for high-temperature bending strength. Study of the oxidation process showed that the weight increment of the 60 wt.% ZrB2 + 20 wt.% SiC + 20 wt.% (Al2O3 + 32 wt.% t-ZrO2) sample at 1600°C for a holding time of 1 h was stabilized by dense oxide scale formed on the material, while the weight increment of the ZrB2 + 20 wt.% SiC sample and, consequently, the scale thickness increased monotonically. The scale that formed on the ZrB2 + 20 wt.% SiC samples with an addition of Al2O3 + 32 wt.% t-ZrO2 consisted of an upper Al2SiO5-based layer 50 μm thick with ZrO2 inclusions and a lower ZrO2-based layer up to 80 μm thick with Al2SiO5 inclusions. The eutectic Al2O3 + 32 wt.% t-ZrO2 oxide addition to the basic ZrB2–SiC system had higher oxidation resistance and thus prevented the diffusion of oxygen into the material.

Self-Propagating High-Temperature Synthesis of Composite Material Based on Stabilized Zirconium Oxide1

Fabrication and Characterization of Y2O3 Stabilized ZrO2 Films Deposited with Aerosol-Assisted MOCVD

Low-Cost Preparation of YSZ-SiC High-Temperature Composite from Zircon and Y2O3 by Carbothermal Reduction

Sintering mechanisms of partially stabilized zirconia (TZ3Y) with ZnO and Co3O4 as sintering additives

Synthesis and thermal stability of zirconia and yttria-stabilized zirconia microspheres

Interaction of Copper Oxide with Zirconium Dioxide Stabilized with Yttrium Oxide

Synthesis of a Nitrided Composite Material from Ferroalumosilicozirconium during Combustion

Effects of CaO Additives on the Phase Evolution of ZrO2-SiC Composites from Zircon by Carbothermal Reduction

Preparation of Al2O3-ZrO2-SiO2 ceramic composites by high-gravity combustion synthesis

Stabilize Consequences of Y2O3 in Zirconia Thermal Barrier Coatings (TBC)

Effect of Yttrium on the Properties of Carbon Fiber-Reinforced ZrB2–SiC Composites

Synthesis and characterization of CaZr0.95In0.05O3 − δ–BaCe0.9Y0.1O3 − θ composite ceramics

A New Type of Precursors for Gas Phase Deposition of Nanostructured Coatings

In Situ Formation of Cu–ZrO2 Composites by Chemical Routes

Co-precipitation Synthesis and Thermal Stability of Zircon Encapsulated Carbon Black

Yttria-stabilized zirconia (8YSZ) synthesis in a supercritical CO 2 -assisted process: a parametric study for achieving cubic phase stability

Components of ceramic composite materials based on organoelement oligomers

Microstructures and phase compositions of Y2O3–ZrO2–HfO2 solid solutions

Thermal decomposition and reaction sintering for synthesis of mullite-zirconia composite using kaolin, γ-alumina and zirconia

Mechanical and Corrosion Properties of ZrB2–SiC Composite Ceramics with Oxide Additions

Fabrication of Ceramic Composites by Microwave Sintering