Abstract:Abstract We have developed a simple method to prepare nano-(ZrC 0.93 , ZrO 2- polymorphs)@carbon composites with graphite/amorphous carbon content and adjustable Zr/C ratio based on using a multistep tube furnace and plasma-assisted heat treatment of zirconium-loaded sulfonated styrene–divinylbenzene (STY-DVB) copolymers. Pre-pyrolysis of zirconium-loaded sulfonated STY-DVB ion exchangers with 2 and 8 mass % DVB at temperatures between 1000 and 1400 °C for 2 h produced nano-ZrO 2 @C intermediates with particle sizes of ~ 30–60 nm with no ZrC formation. Plasma processing of nano-ZrO 2 @C resulted in nano-(ZrC 0.93 , ZrO 2 )@C composites with 11% (under a He atmosphere) (C/Zr = 73) or 13% (under a H 2 atmosphere) (C/Zr = 58) ZrC 0.93 content. Three polymorphs of the zirconium dioxide (tetragonal, monoclinic and cubic, between 18 and 27 nm) were found in the products. The amounts of tetragonal and monoclinic ones are comparable to that of ZrC 0.93 . The average particle size of ZrC 0.93 prepared in this way was found to be 21–23 nm. The BET surface area of the nano-(ZrC 0.93 , ZrO 2 )@C(graphite) composites prepared in He and H 2 was over 250 and 300 m 2 /g, respectively. We developed a reproducible and easy method to prepare nano-(ZrC, ZrO 2 )@C products by setting the DVB content, sulfonation degree, Zr loading and the thermal treatment conditions, which have an influence on the ZrC and graphite/amorphous carbon content of nano-ZrO 2 @C intermediates. The zirconium-loaded sulfonated styrene–divinylbenzene (STY-DVB) copolymers (2 and 8 mass% DVB) or their thermal decomposition was characterized with vibrational spectroscopy, thermal analysis and DSC or powder XRD, BET, XPS and HRTEM methods, respectively.

A New Type of Precursors for Gas Phase Deposition of Nanostructured Coatings

Fabrication and Characterization of Y2O3 Stabilized ZrO2 Films Deposited with Aerosol-Assisted MOCVD

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Role of precursor composition in the polymorph transformations, morphology control and ferromagnetic properties of nanosized TiO$_2$

Phase, microstructure and property evolutions of reactively synthesized YSZ-ZrC composite coating based on the content regulation of the precursor

Self-Propagating High-Temperature Synthesis of Composite Material Based on Stabilized Zirconium Oxide1

Preparation and Flame Ablation Resistance of Al/Zn/Cu-Incorporated Yttria Partially Stabilized Zirconia Coating

Synthesis, spectral characterization and crystal structure of a new precursor [(CH3COCHCOCH3)2Zr{C6H4(N=CHC6H4O)2}] for nano-zirconia: an investigation on the wettability of polyvinylidene fluoride–nano-zirconia composite material

Influence of SHS Precursor Composition on the Properties of Yttria Powders and Optical Ceramics

Facile Synthesis of Highly-dispersed Yttria-doped Zirconia Nanoparticles

Ethanol-induced formation of precursor for 8mol% Yttria-stabilized zirconia: Towards the production of well-dispersed, easily sintering, and high-conductivity nano-powders

TEM Exploration of In-Situ Nanostructured Composite Coating Fabricated by Plasma Spraying 8Ysz-Al-sic Composite Powder

Plasma-assisted preparation of nano-(ZrC, ZrO2)@carbon composites from Zr-loaded sulfonated styrene–divinylbenzene copolymers

Nanostructured Yttria Stabilized Zirconia Coatings Deposited by Air Plasma Spraying

Synthesis and pyrolysis of Hf–N–B backbone polymer precursor for HfC/HfB 2 composite ceramics

Supercritical Hydrothermal Synthesis of Nano-Zirconia: Reaction Path and Crystallization Mechanisms of Different Precursors

Co-precipitation of nano Mg–Y/ZrO2 ternary oxide eutectic system: Effects of calcination temperature

Synthesis of yttria-stabilized zirconia powders for plasma spray by internal gelation

Characterization of the Near-Eutectic Al2O3–40 Wt% ZrO2Composite Coating Fabricated by Atmospheric Plasma Spray. Part I: Preparation and Characterization of Nano Al2O3–ZrO2Powder Using Sol–Gel Method

Mechanochemical dehydration and crystallization of supersaturated zirconia–alumina composite nano powders

Thermal and structural studies of zinc zirconate nanoscale composite derived from sol–gel process