Abstract:Freeze-thaw cycles can damage the microstructure of concrete and reduce the service life of structures, which is particularly detrimental for concrete at very early ages. What size range of pores can be affected by the early-age freeze-thaw cycles and whether the later-age curing can recover the damage to pores are critical questions for understanding the mechanism and avoiding frost damage. Typical low and high water-to-cement (w/c) ratio pastes were investigated experimentally in this study in terms of the pore-size distribution. The pastes were subject to freeze-thaw cycles at the ages of 1 and 7 days and then sealed cured to the age of 40 days for pore-size distribution measurement by the techniques of mercury intrusion porosimetry (MIP), scanning electron microscopy (SEM) with backscattered electron (BSE), and X-ray computer tomography (X-ray CT). The detectable pore-size range by MIP, BSE, and X-ray CT in hardened paste was identified. The pore characteristics within each size range were quantified. It was found that the pores in high w/c ratio=0.5 paste have been coarsened significantly compared to the low w/c ratio=0.3 paste, and the later sealed curing cannot recover the damage. Combination of different techniques can achieve a full-scale quantification of pore size. The total porosity of the samples cannot be directly determined by adding different porosity obtained by different techniques. The results of this study will offer suggestions for material design and curing strategies for concrete structures that are prone to experiencing freeze-thaw cycles at very early ages.

Ink-bottle Effect and Pore Size Distribution of Cementitious Materials Identified by Pressurization–Depressurization Cycling Mercury Intrusion Porosimetry

A reappraisal of the ink-bottle effect and pore structure of cementitious materials using intrusion-extrusion cyclic mercury porosimetry

Pore Structure Damages In Cement-Based Materials By Mercury Intrusion: A Non-Destructive Assessment By X-Ray Computed Tomography

New mercury porosimetry method for the measurement of pore size distribution in cement-based materials

Ink-bottle effect in mercury intrusion porosimetry of cement-based materials

Tracing Mercury Entrapment in Porous Cement Paste after Mercury Intrusion Test by X-ray Computed Tomography and Implications for Pore Structure Characterization

Pore Structure of Cement Pastes Through NAD and MIP Analysis

Analysis of Pore Structure, Contact Angle and Pore Entrapment of Blended Cement Pastes from Mercury Porosimetry Data

Empirical Estimation of Pore Size Distribution in Cement, Mortar, and Concrete

Reassessment of mercury intrusion porosimetry for characterizing the pore structure of cement-based porous materials by monitoring the mercury entrapments with X-ray computed tomography

Characterization of Pore Structure of Cement-based Materials by Water Vapor Sorption Isotherms

Effect of Curing Conditions on Pore Structure of Cement Based Materials

Pore structure characterization of cement pastes blended with high-volume fly-ash

Factors Influencing the Capillary Water Absorption Characteristics of Concrete and Their Relationship to Pore Structure

Investigations on pore-structure in cementitious materials using gas intrusion porosimetry

Critical Features of Microstructure Development of Early-Age Cement Paste Revealed by Non-Contact Electrical Resistivity Measurement

Effect of Epoxy Impregnation on Characterizing Microstructure and Micromechanical Properties of Concrete by Different Techniques

Determining Porosity and Pore Network Connectivity of Cement-Based Materials by a Modified Non-Contact Electrical Resistivity Measurement: Experiment and Theory

Visualization of mercury percolation in porous hardened cement paste by means of X-ray computed tomography

Quantifying Effect of Later Curing on Pores of Paste Subject to Early-Age Freeze-Thaw Cycles by Different Techniques

Computed permeability for cement paste subject to freeze-thaw cycles at early ages