Abstract:Superplasticizers, polyacrylate latexes and asphalt emulsions were employed to investigate the influences of chemical admixtures with different sizes on the pore structure and impermeability of hardened cement pastes. With different admixture types and contents, pore structure and impermeability of specimens cured for 28 days were tested by mercury intrusion porosimetry and alternating current impedance, respectively. Scanning electron microscopy was also used to observe the microstructure of fresh and hardened pastes. The results show that, porosity, average pore size and inkbottle pores volume in the hardened cement pastes as well as permeability presented slight decrease with the increase in the content of superplasticizers. For the specimens with low latex content, the pore size in the hardened cement paste remained unchanged, or was coarsened, and the compactness and impermeability declined; for those with high latex content, the pore size was refined and compactness and impermeability were enhanced. Both of the compactness and impermeability increased with the increase in asphalt emulsion content. At the same content, the latex Ll, having smaller particle size was more effective than latex L2 and, the anionic asphalt emulsion was more effective than cationic asphalt emulsion on improving pore structure and impermeability, respectively. It was accepted that chemical admixtures were able to improve the flowability of fresh paste by enhancing the dispersion of cement grains, further the effects were extended to affect the pore structure and impermeability of hardened one. Meanwhile, the polymer was also effective to compact the interfacial zone between phases by filling up the pore space, which would lead to more compact structure of hardened paste. For the same type of chemical admixture at low content, the pore structure and impermeability were mainly influenced by the dispersion of cement grains, while at high content, the filling effect become dominant. For different types of chemical admixtures with the same filling effect, the better dispersion of cement grains would result in finer pore structure and higher impermeability.

Pore structure characterization of cement pastes blended with high-volume fly-ash

Pore Structure of Cement Pastes Through NAD and MIP Analysis

Surface Fractal Analysis of Pore Structure of High-Volume Fly-Ash Cement Pastes

Study of the Relationship between the Strength of the hydrated Cement Paste with Flyash and its Pore structure

Analysis of Pore Structure, Contact Angle and Pore Entrapment of Blended Cement Pastes from Mercury Porosimetry Data

MICROSTRUCTURAL CHARACTERISTICS OF COMPLEX BINDER PASTE CONTAINING ACTIVE OR INERT MINERAL ADMIXTURES

Influence of fly ash content on alkalinity of pore solution and microstructure of cement pastes

Strength, Permeability and Multiscale Pore Characteristics of Cement-Based Materials with High-Volume Fly Ash Contents and Different Water-Binder Ratios

Characterizing Pore Structure of Cement Blend Pastes Using Water Vapor Sorption Analysis

Critical Features of Microstructure Development of Early-Age Cement Paste Revealed by Non-Contact Electrical Resistivity Measurement

The Microstructure of 4-Year-old Hardened Cement-Fly Ash Paste

Development of Pore Pressure in Cementitious Materials under Low Thermal Effects: Evidence from Optimization of Pore Structure by Incorporation of Fly Ash

Understanding the effect of high-volume fly ash on micro-structure and mechanical properties of cemented coal gangue paste backfill

Microstructure and properties of the binder of fly ash-fluorogypsum-Portland cement

Modification of water absorption and pore structure of high-volume fly ash cement pastes by incorporating nanosilica

Determination of cement hydration and pozzolanic reaction extents for fly-ash cement pastes

Ink-bottle Effect and Pore Size Distribution of Cementitious Materials Identified by Pressurization–Depressurization Cycling Mercury Intrusion Porosimetry

Characterization, factors, and fractal dimension of pore structure of fly ash-based geopolymers

Influences Of Chemical Admixtures With Different Sizes On Pore Structure And Impermeability Of The Hardened Cement

Investigating the Hydration, Mechanical Properties, and Pozzolanic Activity of Cement Paste Containing Co-Combustion Fly Ash

Nanoindentation-based study of the microstructure and degree of hydration in hardened cement paste