Abstract:In order to explore the occurrence area of pervious concrete freeze-thaw deterioration, the mass loss, strength deterioration, ultrasonic longitudinal wave velocity and dynamic elastic modulus attenuation of pervious concrete under freeze-thaw cycles were measured, and a prediction model of freeze-thaw damage was established. The mechanical properties of hardened cement pastes with the same W/C ratio under freeze-thaw cycles were also measured. Mercury intrusion porosimetry (MIP) was used to measure the pore structure characteristic parameters and pore size distribution changes of cement paste under freeze-thaw cycle, and the microstructure evolution of interfacial transition zone (ITZ) of paste and aggregate was observed by SEM scanning electron microscopy. Finally, a pervious concrete model was established by DEM to analyze the relationship between the number of freeze-thaw cycles and the mesoscopic parameters. The results indicated that the quality, strength and dynamic elastic modulus of pervious concrete deteriorate to different degrees under the conditions of water freezing and salt freezing. The damage sensitivity and strength loss of freeze-thaw damage is greater than the dynamic elastic modulus loss, which is greater than mass loss. In the pervious concrete paste which underwent 100 freeze-thaw cycles, the pore structure and macro strength had no obvious change, and hardened paste and the aggregate-interface-generated defects increased with the increase in freezing and thawing times, indicating that the deterioration of pervious concrete performance under freeze-thaw cycles was closely related to the deterioration of the interface strength of the aggregate and hardened paste. The pervious concrete model established by DEM can accurately simulate the change of the compressive modulus and the strength of pervious concrete during freeze-thaw cycles.

Computed permeability for cement paste subject to freeze-thaw cycles at early ages

Quantifying Effect of Later Curing on Pores of Paste Subject to Early-Age Freeze-Thaw Cycles by Different Techniques

Development of Internal Moisture Transfer and Cumulative Residual Strain in Concrete under Freeze-Thaw Cycles

Critical Features of Microstructure Development of Early-Age Cement Paste Revealed by Non-Contact Electrical Resistivity Measurement

A Mathematical Model for the Electrical Resistivity of Cement Paste at Early Ages Considering the Partially Saturated State

Pore structure characterization of cement paste by different experimental methods and its influence on permeability evaluation

Degradation Mechanism and Numerical Simulation of Pervious Concrete under Salt Freezing-Thawing Cycle

Simple Three-Step Analytical Scheme for Prediction of Elastic Moduli of Hardened Cement Paste

Influence of paste coating thickness on the compressive strength, permeability, and mesostructure of permeable concrete

Effect of moisture content on freeze–thaw behavior of cement paste by electrical resistance measurements

Electrical Resistivity of Cement Pastes Undergoing Cyclic Freeze-Thaw Action

Determining Porosity and Pore Network Connectivity of Cement-Based Materials by a Modified Non-Contact Electrical Resistivity Measurement: Experiment and Theory

Prediction of Effective Chloride Diffusivity of Cement Paste and Mortar from Microstructural Features

Pore Structure Damages In Cement-Based Materials By Mercury Intrusion: A Non-Destructive Assessment By X-Ray Computed Tomography

Ink-bottle Effect and Pore Size Distribution of Cementitious Materials Identified by Pressurization–Depressurization Cycling Mercury Intrusion Porosimetry

Empirical Estimation of Pore Size Distribution in Cement, Mortar, and Concrete

Pore Structure of Cement Pastes Through NAD and MIP Analysis

Experimental Study and Analytical Model for Pore Structure of Hydrated Cement Paste

Determination of water permeability for cementitious materials with minimized batch effect

Solid Phases Percolation and Capillary Pores Depercolation in Hydrating Cement Pastes

Development of Micro and Macro Fracture Properties of Cementitious Materials Exposed to Freeze-Thaw Environment at Early Ages