Abstract:Copper oxide thin films were grown on (111)-oriented MgO substrates via the DC magnetron sputtering technique. High-purity copper was used as target material. The films were grown in an atmosphere of pure argon at a pressure of 1.27 torr. The substrate temperature was maintained at 400 °C during the growth. After deposition, the films were annealed in-situ in an argon/oxygen atmosphere (80%/20%) at 450 °C for either two or four minutes. It was found that the annealing time was a sensitive process parameter for achieving single- or mixed-phase copper oxide thin films. The single-phase cuprous (Cu2O) oxide films were obtained with the shorter annealing time (two minutes). Longer annealing times led to destabilization of the Cu2O phase, concomitant with the formation of the cupric oxide (CuO) phase in the sample. From optical spectroscopy studies, a band gap value of 2.4 eV was determined for the Cu2O films. This value decreased for the mixed-phase films. Near-infrared spectroscopy spectra were characterized by the presence of troughs and peaks, probably stemming from volume and surface scattering. Furthermore, differences in the intensity of the absorption with the chosen annealing process were observed, which were probably associated with slight variations in the grain size and/or morphology of the films. The electrical behavior of the films was investigated by means of complex impedance spectroscopy and DC transport measurements. Strong dependence of the electrical properties on the frequency and temperature was observed. The impedance spectra were well modeled in terms of equivalent electrical circuits. As a result, it was found that the predominant contribution to the resistance and capacitance of the Cu2O films came from the bulk of the grains. It was also verified that the relaxation of the charge carriers was a thermally active process with an activation energy of ~ 0.17 eV. A semiconducting-like behavior in the 100–320 K temperature range was also verified. The electronic transport mechanism in the Cu2O films was satisfactorily described within the framework of the Mott variable range hopping model. From the fit of this model to the experimental data, values as high as 3.5 × 1018 eV−1 cm−3 and ~ 12 nm were estimated for the density of states at the Fermi level and the hopping distance, respectively.

Electrical and optical properties of copper oxide thin films prepared by DC magnetron sputtering

Optical and Wetting Properties of CuAlO2 Films Prepared by Radio Frequency Magnetron Sputtering

Oxide phase and conductivity-type of copper oxide thin films deposited by direct current magnetron sputtering

Effect of substrate temperature on the optoelectronic properties of DC magnetron sputtered copper oxide films

Properties of Spray Pyrolysied Copper Oxide Thin Films

On the dielectric properties and conduction mechanism in cuprous oxide thin films grown on (111)-oriented MgO substrates by means of non-reactive DC magnetron sputtering

Study of the structural, optical, electrical and electrochemical properties of copper oxide thin films synthesized by spray pyrolysis

Photo-Catalytic Activity of Cu2O Films with Various Crystal Structures Prepared by DC Reactive Magnetron Sputtering

Optical and Electrical Properties of Copper Oxide Thin Films Synthesized by Spray Pyrolysis Technique

The Optical and Electrical Performance of CuO Synthesized by Anodic Oxidation Based on Copper Foam

Photo-sensing characteristics of CuO thin films synthesized by thermal oxidation of Cu metal films

Oxidation of copper during physical sputtering deposition: mechanism, avoidance and utilization

Study of DC Sputtered Cu2O Growth and P-Cu2o/ N-Igzo Heterojunctions

Preparation and Characterization of Copper Oxide Thin Films Deposited by Filtered Cathodic Vacuum Arc

Annealing temperature induced physical characteristics of CuO films grown by magnetron sputtering

Investigation of sputtering pressure on physical properties of CuO films and the electrical properties-temperature relationship of CuO films and p-CuO/n-GaN heterojunction

Effect of oxygen flow rate ratio on crystalline phase and properties of copper oxide films prepared by room-temperature high-power impulse magnetron sputtering

Influence of Oxygen Flow Rate on the Phase Structures and Properties for Copper Oxide Thin Films Deposited by RF Magnetron Sputtering

Study of Deposition Temperature Effect on Spray-Deposited Copper Oxide Thin Films and Its Schottky Diodes

Effects of anode geometry on DC magnetron sputtering of Copper Oxide films Deposition

Effect of Cu doping on the structural, optical and electrical properties of ZnO thin films grown by RF magnetron sputtering: application to solar photocatalysis