Abstract:<p>For wear resistant steels, there is generally a linear relationship between the initial hardness and wear resistance, yet a high initial hardness limits the formability of components. The intrinsic ductility of austenite and strain hardening produced from the transformation-induced plasticity (TRIP) effect during service opens a new window for this contradiction. Herein, the wear resistance and the corresponding failure mechanisms of 5Mn steels after different heat treatment processes were evaluated using a ball-on-disk sliding test under dry conditions. The wear behaviors of the counterbodies were also studied to elucidate the wear mechanism of the tribo-system. The results show that the microstructures of the hot-rolled and air-cooled steel mainly comprised martensite. When the intercritical annealing temperature was relatively low (<695°C), the microstructure primarily consisted of reversed austenite and ferrite. The samples annealed at 630°C, 645°C, 660°C, and 675°C had a similar initial hardness, while the sample annealed at 675°C possessed a wear resistance that was 3.25 times that of the steel annealed at 630°C. The large difference in the wear resistance was predominately due to the gradient of strain hardening provided by the varied amount and mechanical stability of the retained austenite. The transformation from austenite to martensite, which has an increased hardness, improves the work hardening. A strengthening layer formed with a certain thickness that provided stress support during the wear process and enhanced the wear resistance. When the annealing temperature reached 695°C, a large amount of secondary martensite was generated from austenite that had a low thermal stability, which improved the initial hardness and wear resistance. The steels with a large amount of martensite had an enhanced wear resistance, but the elongation severely deteriorated, leading to unsatisfactory formability. The present work provides guidance for designing novel steels with an excellent balance of good formability and decent wear resistance by precisely adjusting the characteristics of the retained austenite.</p>

Investigation on Microstructure and Properties of Low‐Carbon Wear‐Resistant Steels with Addition of Cr and Ni

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Influences of Partial Substitution of C by N on the Microstructure and Mechanical Properties of 9cr18mo Martensitic Stainless Steel

Influence of Ni content on impact-abrasion wear resistance of medium-carbon low alloy cast steel

Surface self-nanocrystallization and -lubricating dependent wear resistance of austenitic steels at same initial hardness level

The alloying effects of Cr on in-situ phase evolution and wear resistance of nickel composite coatings fabricated by wide-band laser deposition

Dry Sliding Wear Properties of Annealed Carbon Steels Matrix Composites by Nano‐Sized TiC‐TiB2 Particles

The Influence of Cr Addition on the Microstructure and Mechanical Properties of Fe-25Mn-10Al-1.2C Lightweight Steel

The Microstructure Transformations and Wear Properties of Nanostructured Bainite Steel with Different Si Content

The Effect of N Content on the Microstructure and Wear Resistance of Improved High-Carbon Chromium Bearing Steel

Microstructure, Mechanical Properties and Wear Resistance of Low Alloy Abrasion Resistant Martensitic Steel Reinforced with TiC Particles

EFFECT OF CrMoN HARD COATINGS WITH DIFFERENT COM-POSITIONS ON THE SURFACE PROPERTIES OF DIE STEELS

Enhancing the adhesion strength and wear resistance of nanostructured NiCrN coatings

Study on the role of chromium addition on sliding wear and corrosion resistance of high-manganese steel coating fabricated by wire arc additive manufacturing

Simultaneous improvement of corrosion and wear resistance of Fe–Mn–Al–C lightweight steels: The role of Cr/Mo

Study on the microstructure and wear resistance of laser cladding layer of Ni and Cr on the surface of stainless steel

Influence of WC grain size on the microstructure and wear property enhancement of 18Ni300 coatings

Unraveling the significant role of retained austenite on the dry sliding wear behavior of medium manganese steel

Study of Cracking Mechanism and Wear Resistance in Laser Cladding Coating of Ni-based Alloy

Microstructure and Mechanical Properties of Chromium-Alloyed Silicon Cast Steel

Superior wear resistance of dual-phased TiC–TiB2 ceramic nanoparticles reinforced carbon steels