Abstract:As a commonly reinforcing phase in wear-resistant materials, TiC is often added into wear-resistant materials to improve the wear resistance. The independently developed stepped molds with variable thicknesses were used to prepare the TiC-reinforced steels with the same composition though melt solidification processing to study the effect of the solidification rate on the particle size and wear performance. The effect of the hot rolling compression ratio on the particle size and wear performance was also studied. The length and aspect ratios of the particles in heat-treated TiC-reinforced steels with different billet thicknesses and rolling compression ratios were measured. With the increasing in the billet thickness and the decreasing in the rolling compression ratio, the length and aspect ratio of the particles increased in heat-treated TiC-reinforced steels, and the hardness decreased slightly. The three-body abrasive wear behavior of the TiC-reinforced steels was conducted using a standard dry sand rubber wheel wear testing procedure, and the modeling of the wear mechanism was established. The particle size is the main factor affecting wear resistance when the hardness of TiC-reinforced steels is similar. When the particles size is moderate, about 2–6 μm, the particle can break the sand tip and hinder the sand tip from sliding on the surface. In this manner, the mass loss decreased and the wear resistance improved. The large particles will be broken easily by the abrasive, and the small particles are removed easily by the abrasive in the wear process. So, the large and small particles cannot effectively prevent the damage of the abrasive to the matrix, and they have less of an effect on improving wear resistance.

Dry Sliding Wear Properties of Annealed Carbon Steels Matrix Composites by Nano‐Sized TiC‐TiB2 Particles

Dry Sliding Wear Properties of Annealed Carbon Steels Matrix Composites by Nanosized TiC‐TiB2 Particles

Superior wear resistance of dual-phased TiC–TiB2 ceramic nanoparticles reinforced carbon steels

Microstructure, Mechanical Properties and Wear Resistance of Low Alloy Abrasion Resistant Martensitic Steel Reinforced with TiC Particles

Synergistic optimization in microstructure and mechanical properties of low carbon steel via trace amount of nano-sized TiC-TiB2

Dry sliding wear behavior of in situ Cu–TiB2 nanocomposites against medium carbon steel

Tribological behavior of in-situ nanosized TiB2 particles reinforced AZ91 matrix composite

Achieving high strength and superior wear‐resistant properties in TiH2 matrix reinforced with graphene nanoplates

A Novel Design to Enhance the Tribological Properties of High‐Cr Hot Work Die Steel via Trace TiC Ceramic Nanoparticles

Application of ceramic nanoparticles in microstructure manipulation and simultaneously strengthening toughness and wear resistance of tool and die steels

Abrasive Wear and Physical Properties of In-Situ Nano-TiCx Reinforced Cu–Cr–Zr Composites

Tuning composition and microstructure by doping Ti and C for enhancing mechanical property and wear resistance of Al0.2Co1.5CrFeNi1.5Ti0.5 high entropy alloy matrix composites

Preparation and Characterization of In Situ (TiC-TiB2)/Al-Cu-Mg-Si Composites with High Strength and Wear Resistance

Dry Sliding Friction and Wear Behavior of Cu-Nanosized TiB2 In-situ Composites

Microstructure and Wear Resistance of a Composite Coating Prepared by Laser Alloying with Ni-Coated Graphite on Ti-6Al-4V Alloy

Microstructure and tribological properties of Al 7075-TiO2@CNTs composites under T6 treatment

Effect of Solidification and Hot Rolling Processes on Wear Performance of TiC-Reinforced Wear-Resistant Steel

Microstructure and Wear Behaviour of Ceramic Particles Strengthening Nial Based Composite

Improved wear resistance of TiAl composite coatings through NbC@(Ti,Nb) 2 AlC core-shell structure and nanoscale precipitation strengthening

Wear Behavior of Ti6Al4V Based Hybrid Composites Reinforced with TiB2(7.5%) + TiC (7.5%)

Simultaneously enhanced strength and toughness of cast medium carbon steels matrix composites by trace nano-sized TiC particles