Abstract:In this paper, Cu thin films were deposited on Si (100) substrates by the high-power impulse magnetron sputtering (HiIPMS) technique, and the effects of different duty cycles (from 2.25% to 5.25%) on the plasma discharge characteristics, microstructure, and electrical properties of Cu thin films were investigated. The results of the target current test show that the peak target current remains stable under 2.25% and 3% duty cycle conditions. Under the conditions of a 4.5% and 5.25% duty cycle, the target peak current shows a decreasing trend. The average power of the target shows a rising trend with the increase in the duty cycle, while the peak power of the target shows a decreasing trend with the increase in the duty cycle. The results of OES show that with the increase in the duty cycle, the total peak intensity of copper and argon emissions shows an overall increasing trend. The duty cycle from 3% to 4.5% change in copper and argon emission peak total intensity change is not obvious. The deposition rate and surface morphology of the copper film were investigated by scanning electron microscopy, and the deposition rate of the copper film increased with the increase in the duty cycle, which was mainly due to the increase in the average power. The surface roughness of the copper film was evaluated by atomic force microscopy. X-ray diffraction (XRD) was used to analyze the grain size and texture of the Cu film, and the results showed that the average grain size of the Cu film increased from 38 nm to 59 nm on the (111) and (200) crystal planes. Four-probe square resistance test copper film resistivity in 2.25%, 3% low duty cycle conditions of the copper film resistivity is generally higher than 4.5%, 5.25% high duty cycle conditions, the copper film resistivity shows the trend of change is mainly affected by the copper film grain size and the (111) face of the double effect of the optimal orientation. The lowest resistivity of the copper film measured under the 4.5% duty cycle condition is 1.7005 μΩ·cm, which is close to the intrinsic resistivity of the copper film of 1.67 μΩ·cm.

Effect of the Pulse Duty Cycle on the Microstructure and Properties of a Jet Electrodeposited Nanocrystalline Copper Coating

Surface morphology and crystal orientation of electrodeposited tungsten coatings with different pulse parameters

Strategies to Achieve High Strength and Ductility of Pulsed Electrodeposited Nanocrystalline Co-Cu by Tuning the Deposition Parameters

Preparation and Investigation of Ni–Co–P Alloy Coatings Using Jet Electrodeposition with Varying Pulse Parameters

Influence of Pulse Current Forward-Reverse Duty Cycle on Structure and Performance of Electroplated W–Cu Composite Coatings

Effects of Pulse Parameters on Macro-Particle Production in Pulsed Cathodic Vacuum Arc Deposition

Investigation on the effect of nickel and nickel-chromium alloy pulse current plating on copper substrate

Effect of duty cycle on microstructure and mechanical properties of AlCrN coatings deposited by HiPIMS

Effects of HiPIMS Duty Cycle on Plasma Discharge and the Properties of Cu Film

Effect of Pulse Electrodeposition Mode on Microstructures and Properties of Ni-TiN Composite Coatings

Effect of Duty Cycle on the Corrosion Resistance and Hardness of Ni-WC Nano-composite Coatings

Microstructure and Properties of TiN/TiCN/Al2O3/TiN Coating Enhanced by High-Current Pulsed Electron Beam

Structure and corrosion property of pulse electrodeposited nanocrystalline nickel-tungsten-copper alloy coating

Mechanism of copper electrodeposition by pulse current and its relation to current efficiency

Studies on Pitting Corrosion of Pulsed Electrodeposited Nanocomposite Coating

Effect of Electropulsing Treatment on the Fatigue Crack Growth Behavior of Copper

Study of the Effect of Current Density on the Metallurgical Properties of AlFeCrNiTi High Entropy Alloy Coating Produced by Pulse Plating

Effects of duty cycle on microstructure and mechanical properties of (AlCrNbSiTi)N high-entropy nitride hard coatings deposited by pulsed arc ion plating

Microstructure control of ultra-high-strength AlZnMgCu alloys fabricated by wire arc directed energy deposition: the role of variable polarity electric pulse

Effect Of Pulsed Current On Mechanical And Anticorrosion Properties Of Laser Cladded Coating

Effect of additives on the microstructure and properties of pulsed electrodeposited copper foils