Abstract:Co–Cr–Fe–Mn–Ni high-entropy alloy thin films were synthesized by pulse electrochemical deposition method. The films were co-deposited in an electrolyte based on a DMF-CH3CN organic system consisting of Co, Cr, Fe, Mn, and Ni cations via the pulse electrodeposition method at 2500 and 5000 Hz frequencies, as well as 50% and 60% duty cycles. The GXRD patterns indicated that films consisted of a single face-centered-cubic structure. The effect of pulsed electrodeposition parameters on wettability and corrosion resistance of coatings was investigated as well. The results of the hydrophobic/hydrophilic test showed that all coatings were completely hydrophilic; the largest wettability angle is for the prepared film at a duty cycle of 50% in frequency of 5000 Hz (56°). The potentiodynamic polarization test results showed that same sample with a corrosion density of 0.067 μA/cm2, improved the corrosion resistance of the substrate due to the superhydrophilic properties of those by about 34 times, and therefore, was chosen as optimal conditions. Also, it was shown that none of the samples were sensitive to pitting corrosion. The results of the EIS test showed an outstanding performance of coatings in improving corrosion resistance compared to similar alloy samples, with a conservation efficiency of about 95%. In addition, it enables the evaluation of continuous changes in the metal-coating system. In such conditions, prepared film at 50% duty cycle in frequency of 5000 Hz improved the corrosion resistance of the substrate by about 40 times.<h3 class="a-plus-plus">Graphic </h3>

Preparation and Investigation of Ni–Co–P Alloy Coatings Using Jet Electrodeposition with Varying Pulse Parameters

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

Process for Nickel-Phosphorous Pulse Electroplating and Corrosion Resistance of the Alloy Coating

Effect of Cobalt Content on the Properties of Nickel-Cobalt Alloy Coatings

Preparation and Properties of Textured Ni–W Coatings Electrodeposited on the Steel Surface from a Pyrophosphate Bath

Effects of deposition current density, time and scanning velocity on scanning jet electrodeposition of Ni-Co alloy coating

The Influence of Pulse Plating Parameters on the Structure and Corrosion Behavior of Ni-W-TiC Nanocomposite Coatings

Effect of Pulse Electrodeposition Mode on Microstructures and Properties of Ni-TiN Composite Coatings

Synthesis and Evaluation of Pulse Current and Direct Current Electroplating Ni-W Coatings on Steel

Effect of the Pulse Duty Cycle on the Microstructure and Properties of a Jet Electrodeposited Nanocrystalline Copper Coating

Synthesis and characterization of amorphous NiCoP alloy films by magnetic assisted jet electrodeposition

Electrodeposition and corrosion performance of Ni-Co alloys with different cobalt contents

Influence of Electrodeposition Process Parameters and Si3N4 Nanoparticle Concentration on Microhardness and Wettability of Ni-Co-Si3N4 Nanocomposite Coatings

Preparation and characterization of Ni-P-Al2O3-PTFE nanocomposite coatings by unidirectional jet electrodeposition

Tribological performance of Ni-W/PTFE composite coating via pulse electrodeposition

Pulsed electroplating of ZrO2-reinforced Ni-Cr alloy coatings from the duplex complexing agents-containing bath for engineering applications: Importance of operating conditions

Characterization of Co–Cr–Fe–Mn–Ni High-Entropy Alloy Thin Films Synthesized by Pulse Electrodeposition: Part 2: Effect of Pulse Electrodeposition Parameters on the Wettability and Corrosion Resistance

Pulse electrodeposited Ni–C films and its performance

The influence of electrodeposited Ni-Co alloy coating microstructure on CO2 corrosion resistance on X65 steel

Structure and corrosion property of pulse electrodeposited nanocrystalline nickel-tungsten-copper alloy coating

Corrosion Studies on Pulse Reverse Ni-Mo Coatings Electrodeposited on Cu Substrate