Abstract:Magnesia-chrome refractories have been essential materials for application as wear lining in copper production furnaces for many years. Formation of hexavalent chromium (Cr(VI)) has been a major concern despite its admirable corrosion resistance in copper slag. Magnesia-chrome refractory specimens (9, 12, 15 and 18 wt% Cr2O3) with addition of Al2O3 and TiO2 were fabricated and subsequent corrosion tests using copper slag was conducted in air. The corrosion mechanism between magnesia-chrome refractories fabricated and synthetic copper slag were investigated by means of X-ray diffraction (XRD) and scanning electron microscope (SEM), and concurrent formations of Cr(VI) were assessed effectively by leaching test. All the magnesia-chrome specimens prepared are composed of periclase and composite spinel Mg(Al,Cr,Ti)(2)O-4 phases after firing at 1700 degrees C. Densification of the specimens decreases with the increase in Cr2O3 content due to the increased volume expansion, while TiO2 addition can improve their densification as mass transfer is enhanced during the sintering process. The corrosion resistance of the specimens decreases slightly with the Cr2O3 content due to the increased apparent porosity, which would result in penetration of more corrosive slag at the initial stage of the corrosion test while a newly formed (Mg,Cu)(Cr,Fe)(2)O-4 spinel dense layer between the slag and penetration layer effectively hinders further penetration of slag and well protects the specimens. The Cr(VI) in the specimens prepared increases obviously with the Cr2O3 added content, while the TiO2 addition can suppress the formation of Cr(VI) effectively and the copper slag can cause the formed Cr(VI) to be reduced further during the corrosion process. For all the specimens, concentrations of Cr(VI) in the leachates is much lower than the US-EPA limit of 100 mg/kg but exceeds the European limit of 2 mg/kg after the corrosion test. (C) 2019 Elsevier B.V. All rights reserved.

Mechanism of Periclase-Chromite Refractory Breakdown Under Acid Slag Action

The mechanism of destruction of periclase-chromite refractories under the influence of acidic slag

Comparative Study of Chromite-Periclase and Periclase-Carbon Refractory Stability During Reaction with Nickel Production Melts (Experimental Data). 2. Behavior of Periclase-Carbon Refractories in the Presence of Metal-Slag and Slag Melts

Comparative Study of Chromite-Periclase and Periclase-Carbon Refractory Stability During Reaction with Nickel Production Melts (Experimental Data). 1. Behavior of Chromite-Periclase Refractories in the Presence of Metal-Slag and Slag Melts

Corrosion behavior and failure mechanism of amorphous Al2O3 coating at high-temperature LBE

Composition and microstructure of a periclase–composite spinel brick used in the burning zone of a cement rotary kiln

Corrosion mechanism of Al2O3–SiC–C refractory by SiO2–MgO-based slag

Corrosion Mechanism of Alumina-Chromia Refractory by SiO2-Al2O3-CaO Based Slag from Iron Capture Process of Spent Automotive Catalyst

Corrosion mechanism of cement-bonded Al2O3–MgAl2O4 pre-cast castables in contact with molten steel and slag

Microstructure evolution, mechanical characteristics and erosion behavior of Cr2O3–Al2O3–MgO–ZrO2 refractories in molten reduction slag

Corrosion Behavior of BF Slag to SiAlON Bonded Corundum Refractories

Interactions of high-chromia refractory materials with infiltrating coal slag in the oxidizing atmosphere of a cyclone furnace

Degradation behaviors of cement-free corundum-spinel castables in Ruhrstahl Heraeus refining ladle: Role of infiltrated steel

Comparison of corrosion behavior of primary/modified nickel slag with semi‐rebonded periclase‐chromite refractory

Corrosion of high-chrome refractory materials by high-sodium slag in an entrained-flow gasifier

Corrosion Resistance of MgO and Cr2O3-Based Refractory Raw Materials to PbO-Rich Cu Slag Determined by Hot-Stage Microscopy and Pellet Corrosion Test

Regulating the pore structure of periclase refractories by adding Y2O3 to enhance corrosion resistance for copper slag

Corrosion in high alumina refractory serviced in a bench-scale entrained flow gasifier

Corrosion behavior of CaO–Al2O3–SiO2–MgO-Cr2O3 slag on MgO refractory brick for smelting of chromite

Corrosion Mechanisms of Magnesia-Chrome Refractories in Copper Slag and Concurrent Formation of Hexavalent Chromium

Formation of ferrospinel layer at the corroded interface between Al 2 O 3 ‐spinel refractory and molten steel in RH refining ladle