Abstract:Magnesia-chrome refractories have been essential materials for application as wear lining in copper production furnaces for many years. Formation of hexavalent chromium (Cr(VI)) has been a major concern despite its admirable corrosion resistance in copper slag. Magnesia-chrome refractory specimens (9, 12, 15 and 18 wt% Cr2O3) with addition of Al2O3 and TiO2 were fabricated and subsequent corrosion tests using copper slag was conducted in air. The corrosion mechanism between magnesia-chrome refractories fabricated and synthetic copper slag were investigated by means of X-ray diffraction (XRD) and scanning electron microscope (SEM), and concurrent formations of Cr(VI) were assessed effectively by leaching test. All the magnesia-chrome specimens prepared are composed of periclase and composite spinel Mg(Al,Cr,Ti)(2)O-4 phases after firing at 1700 degrees C. Densification of the specimens decreases with the increase in Cr2O3 content due to the increased volume expansion, while TiO2 addition can improve their densification as mass transfer is enhanced during the sintering process. The corrosion resistance of the specimens decreases slightly with the Cr2O3 content due to the increased apparent porosity, which would result in penetration of more corrosive slag at the initial stage of the corrosion test while a newly formed (Mg,Cu)(Cr,Fe)(2)O-4 spinel dense layer between the slag and penetration layer effectively hinders further penetration of slag and well protects the specimens. The Cr(VI) in the specimens prepared increases obviously with the Cr2O3 added content, while the TiO2 addition can suppress the formation of Cr(VI) effectively and the copper slag can cause the formed Cr(VI) to be reduced further during the corrosion process. For all the specimens, concentrations of Cr(VI) in the leachates is much lower than the US-EPA limit of 100 mg/kg but exceeds the European limit of 2 mg/kg after the corrosion test. (C) 2019 Elsevier B.V. All rights reserved.

Comparative Study of Chromite-Periclase and Periclase-Carbon Refractory Stability During Reaction with Nickel Production Melts (Experimental Data). 1. Behavior of Chromite-Periclase Refractories in the Presence of Metal-Slag and Slag Melts

Comparative Study of Chromite-Periclase and Periclase-Carbon Refractory Stability During Reaction with Nickel Production Melts (Experimental Data). 2. Behavior of Periclase-Carbon Refractories in the Presence of Metal-Slag and Slag Melts

Comparison of corrosion behavior of primary/modified nickel slag with semi‐rebonded periclase‐chromite refractory

Mechanism of Periclase-Chromite Refractory Breakdown Under Acid Slag Action

Chemical and Phase Reactions on the Contact between Refractory Materials and Slags, a Case from the 19th Century Zn-Pb Smelter in Ruda Śląska, Poland

The mechanism of destruction of periclase-chromite refractories under the influence of acidic slag

Corrosion Resistance of MgO and Cr2O3-Based Refractory Raw Materials to PbO-Rich Cu Slag Determined by Hot-Stage Microscopy and Pellet Corrosion Test

Corrosion behavior of CaO–Al2O3–SiO2–MgO-Cr2O3 slag on MgO refractory brick for smelting of chromite

Study on the stability of different refractories during the melting process of a K4169 Ni-based superalloy

Chromium Recovery from Ferro-Chromium Slags

Corrosion Mechanisms of Magnesia-Chrome Refractories in Copper Slag and Concurrent Formation of Hexavalent Chromium

Phase Equilibria Study of the MgO–CaO–SiO2 Slag System with Ferronickel Alloy, Solid Carbon, and Al2O3 Additions

Assessing Magnesia Effect on Preparing Refractory Materials from Ferrochromium Slag

Chromium-promoted preparation of forsterite refractory materials from ferronickel slag by microwave sintering

Effect Of Roasting Temperature On Phase Transformation In Co-Reduction Roasting Of Nickel Slag

Corrosion of MgO–C Refractory with Ladle Slags

Experimental Determination of the Main Parameters of the Refining Process of Rough Ferronickel, Obtained by Iron-Chromium-Nickel Selective Reduction

Corrosion Mechanism of Alumina-Chromia Refractory by SiO2-Al2O3-CaO Based Slag from Iron Capture Process of Spent Automotive Catalyst

The development of a thermodynamic model for Al2O3–MgO refractory castable corrosion by secondary metallurgy steel ladle slags

High-temperature tensile strength of alumina-spinel refractory by Brazilian test at 1200 o C coupled with DIC in-situ monitoring

Microstructure evolution, mechanical characteristics and erosion behavior of Cr2O3–Al2O3–MgO–ZrO2 refractories in molten reduction slag