Abstract:Magnesia-chrome refractories have been essential materials for application as wear lining in copper production furnaces for many years. Formation of hexavalent chromium (Cr(VI)) has been a major concern despite its admirable corrosion resistance in copper slag. Magnesia-chrome refractory specimens (9, 12, 15 and 18 wt% Cr2O3) with addition of Al2O3 and TiO2 were fabricated and subsequent corrosion tests using copper slag was conducted in air. The corrosion mechanism between magnesia-chrome refractories fabricated and synthetic copper slag were investigated by means of X-ray diffraction (XRD) and scanning electron microscope (SEM), and concurrent formations of Cr(VI) were assessed effectively by leaching test. All the magnesia-chrome specimens prepared are composed of periclase and composite spinel Mg(Al,Cr,Ti)(2)O-4 phases after firing at 1700 degrees C. Densification of the specimens decreases with the increase in Cr2O3 content due to the increased volume expansion, while TiO2 addition can improve their densification as mass transfer is enhanced during the sintering process. The corrosion resistance of the specimens decreases slightly with the Cr2O3 content due to the increased apparent porosity, which would result in penetration of more corrosive slag at the initial stage of the corrosion test while a newly formed (Mg,Cu)(Cr,Fe)(2)O-4 spinel dense layer between the slag and penetration layer effectively hinders further penetration of slag and well protects the specimens. The Cr(VI) in the specimens prepared increases obviously with the Cr2O3 added content, while the TiO2 addition can suppress the formation of Cr(VI) effectively and the copper slag can cause the formed Cr(VI) to be reduced further during the corrosion process. For all the specimens, concentrations of Cr(VI) in the leachates is much lower than the US-EPA limit of 100 mg/kg but exceeds the European limit of 2 mg/kg after the corrosion test. (C) 2019 Elsevier B.V. All rights reserved.

Comparative Study of Chromite-Periclase and Periclase-Carbon Refractory Stability During Reaction with Nickel Production Melts (Experimental Data). 2. Behavior of Periclase-Carbon Refractories in the Presence of Metal-Slag and Slag Melts

Comparative Study of Chromite-Periclase and Periclase-Carbon Refractory Stability During Reaction with Nickel Production Melts (Experimental Data). 1. Behavior of Chromite-Periclase Refractories in the Presence of Metal-Slag and Slag Melts

Comparison of corrosion behavior of primary/modified nickel slag with semi‐rebonded periclase‐chromite refractory

Mechanism of Periclase-Chromite Refractory Breakdown Under Acid Slag Action

The mechanism of destruction of periclase-chromite refractories under the influence of acidic slag

Effect of Calcium Aluminate-Based Additive on Properties of Periclase-Carbon Refractories for Steel-Teeming Ladles

Corrosion Resistance of MgO and Cr2O3-Based Refractory Raw Materials to PbO-Rich Cu Slag Determined by Hot-Stage Microscopy and Pellet Corrosion Test

Corrosion behavior of CaO–Al2O3–SiO2–MgO-Cr2O3 slag on MgO refractory brick for smelting of chromite

Chemical and Phase Reactions on the Contact between Refractory Materials and Slags, a Case from the 19th Century Zn-Pb Smelter in Ruda Śląska, Poland

Study on the stability of different refractories during the melting process of a K4169 Ni-based superalloy

Corrosion Mechanisms of Magnesia-Chrome Refractories in Copper Slag and Concurrent Formation of Hexavalent Chromium

Chromium Recovery from Ferro-Chromium Slags

Corrosion Mechanism of Alumina-Chromia Refractory by SiO2-Al2O3-CaO Based Slag from Iron Capture Process of Spent Automotive Catalyst

Effects of different particle size of spinel and Y2O3 additive of the periclase-spinel refractory on the sintering densification and corrosion resistance to copper smelting slag

Composition and microstructure of a periclase–composite spinel brick used in the burning zone of a cement rotary kiln

Study of the Effect of Impregnation on Clinker Resistance of High-Purity Periclase-Spinel Refractories

Microstructure evolution, mechanical characteristics and erosion behavior of Cr2O3–Al2O3–MgO–ZrO2 refractories in molten reduction slag

Corrosion of MgO–C Refractory with Ladle Slags

Corrosion mechanism of magnesia-chrome refractory bricks with FetO-SiO2-Cr2O3 copper converter slag

Effects of Cr2O3 Content on Microstructure and Mechanical Properties of Al2O3 Matrix Composites

Microstructure, phase evolution, mechanical properties and slag corrosion resistance of ZrO2 reinforced Al2O3–Cr2O3 composites