Abstract:AISI 52100 steel has been widely used in the mechanical industry due to its excellent mechanical properties and high availability. In some cases, an ultra-smooth surface of AISI 52100 steel is needed and is even indispensable for the satisfactory performance of devices. In this paper, chemical mechanical polishing technique was employed to prepare the ultra-smooth surface of AISI 52100 steel. Colloidal silica was used as the abrasive. The effects of pH, complexing agent such as glycine, H2O2 and benzotriazole (BTA) on the polishing performance were studied. It is revealed that, with the increase of pH, the static etching rate (SER) and the material removal rate (MRR) are both gradually reduced, and the post-CMP surface roughness I?, decreases. This is attributed to the fact that compact and passive iron oxides, especially Fe(III) oxides, gradually form on the top surface. At pH 4.00, in the presence of glycine, and with the increase of the H2O2 concentration, the SER is further suppressed, and the surface roughness R-a gradually decreases; the MRR initially dramatically increases due to the fact that, with the addition of small amount of H2O2, the porous iron oxide layer with relatively low mechanical strength can be rapidly formed on the surface. Moreover, glycine intensifies the chemical dissolution by chelating iron ions, especially Fe(II) ions, and thereby the mechanical strength of the oxide layer further weakens. Then, after reaching the peak value, the MRR gradually decreases when the H2O2 concentration further increases since the compactness of the oxide layer gradually increases. With the increase of the BTA concentration, the MRR is gradually suppressed and the surface roughness R-a decreases due to the formation of Fe-BTA passivating film on the top surface. Finally, a two-step polishing process was developed. The polishing results show that, within 20 min, a rough surface of AISI 52100 steel with the R-a value of 188 nm can be polished into an ultra-smooth surface with the R-a value of 1.8 nm. (C) 2015 Elsevier B.V. All rights reserved.

Potassium persulfate as an effective oxidizer for chemical mechanical polishing of GCr15 bearing steel

Enhancing Chemical Mechanical Polishing Efficiency of Steel with Sulfate

Barrier And Low K Polish With A Novel Alkaline Barrier Slurry Combining With Fa/O Chelating Agent

Novel Eco-friendly Slurries for Chemical Mechanical Polishing of GCr15 Bearing Steel

Chemical Mechanical Polishing of Steel Substrate Using Colloidal Silica-Based Slurries

Achieving a super-smooth surface of stainless bearing steel with chemical mechanical polishing via controlling corrosive wear of Fe and Cr

Electrochemical Analysis of the Slurry Composition for Chemical Mechanical Polishing of Flexible Stainless-Steel Substrates

Chemical Mechanical Polishing of Molybdenum in Potassium Iodate-Based Acidic Slurries

Effects of Ph and Oxidizer on Chemical Mechanical Polishing of Aisi 1045 Steel

High-performance chemical mechanical polishing slurry for aluminum alloy using hybrid abrasives of zirconium phosphate and alumina

Effects of KIO 4 concentration and pH values of the solution relevant for chemical mechanical polishing of ruthenium

Potassium persulfate as an oxidizer in chemical mechanical polishing slurries relevant for copper interconnects with cobalt barrier layers

Effect of Potassium Ferrocyanide on CMP Performance of Ruthenium in H 2 O 2 -based Slurries

Improvement in chemical mechanical polishing of 4H-SiC wafer by activating persulfate through the synergistic effect of UV and TiO2

Study of the polishing slurry dispersant for chemical mechanical polishing of 304 stainless steel

Chemical mechanical polishing of silicon wafers using developed uniformly dispersed colloidal silica in slurry

A novel process of chemical mechanical polishing for FV520B steel

Tribocorrosion Study of Copper During Chemical Mechanical Polishing in Potassium Periodate-Based Slurry

Surface Characteristics of Ruthenium in Periodate-Based Slurry During Chemical Mechanical Polishing

Chemical Mechanical Polishing of Aluminum Alloys using Alumina-Based Slurry

Chemical Mechanical Polishing of Copper in Organic Phosphonic Acid System Slurry