Abstract:AISI 52100 steel has been widely used in the mechanical industry due to its excellent mechanical properties and high availability. In some cases, an ultra-smooth surface of AISI 52100 steel is needed and is even indispensable for the satisfactory performance of devices. In this paper, chemical mechanical polishing technique was employed to prepare the ultra-smooth surface of AISI 52100 steel. Colloidal silica was used as the abrasive. The effects of pH, complexing agent such as glycine, H2O2 and benzotriazole (BTA) on the polishing performance were studied. It is revealed that, with the increase of pH, the static etching rate (SER) and the material removal rate (MRR) are both gradually reduced, and the post-CMP surface roughness I?, decreases. This is attributed to the fact that compact and passive iron oxides, especially Fe(III) oxides, gradually form on the top surface. At pH 4.00, in the presence of glycine, and with the increase of the H2O2 concentration, the SER is further suppressed, and the surface roughness R-a gradually decreases; the MRR initially dramatically increases due to the fact that, with the addition of small amount of H2O2, the porous iron oxide layer with relatively low mechanical strength can be rapidly formed on the surface. Moreover, glycine intensifies the chemical dissolution by chelating iron ions, especially Fe(II) ions, and thereby the mechanical strength of the oxide layer further weakens. Then, after reaching the peak value, the MRR gradually decreases when the H2O2 concentration further increases since the compactness of the oxide layer gradually increases. With the increase of the BTA concentration, the MRR is gradually suppressed and the surface roughness R-a decreases due to the formation of Fe-BTA passivating film on the top surface. Finally, a two-step polishing process was developed. The polishing results show that, within 20 min, a rough surface of AISI 52100 steel with the R-a value of 188 nm can be polished into an ultra-smooth surface with the R-a value of 1.8 nm. (C) 2015 Elsevier B.V. All rights reserved.

Effects of Ph and Oxidizer on Chemical Mechanical Polishing of Aisi 1045 Steel

Chemical Mechanical Polishing of Steel Substrate Using Colloidal Silica-Based Slurries

Potassium persulfate as an effective oxidizer for chemical mechanical polishing of GCr15 bearing steel

Effects of Ceria Abrasives on the Chemical Mechanical Polishing of Molybdenum Film with Alkaline H2O2 Slurries

Structure-Performance Relationships of Complexing Agents on the Chemical Mechanical Polishing of 6063 Aluminum Alloy

Chemical Mechanical Polishing of Stainless Steel As Solar Cell Substrate

Effect of pH on Material Removal Rate of Cu in Abrasive-Free Polishing

Chemical Mechanical Polishing of Mo Using H2O2 as Oxidizer in Colloidal Silica Based Slurries

Enhancing Chemical Mechanical Polishing Efficiency of Steel with Sulfate

Oxidation Anisotropy of 4H-Sic Wafers During Chemical-Mechanical Polishing

Electrochemical polishing versus mechanical polishing of AISI 304: surface and electrochemical study

Effects of pH Values and H2O2 Concentrations on the Chemical Enhanced Shear Dilatancy Polishing of Tungsten

Counterion-Driven Mechanochemical Reactions at TC4 Alloy/SiO2 Interfaces: Electrical Double Layer and Dynamic Ionic Radius

Exploiting the effect of PEO parameters on the surface of AISI 1020 low-carbon steel treated in a TaOH-rich electrolyte

Achieving a super-smooth surface of stainless bearing steel with chemical mechanical polishing via controlling corrosive wear of Fe and Cr

The influence of pH and H2O2 on surface quality and material removal rate during W-CMP

Effect of Oxidant Concentration on the Oxide Layer Thickness of 304 Stainless Steel

Effects of corrosion environments on the surface finishing of copper chemical mechanical polishing

Chemical Mechanical Polishing of Copper in Organic Phosphonic Acid System Slurry

Study on Chemical Action Mechanism of Ferric Chloride-Based Polishing Slurry in CMP of 304 Stainless Steel

The Effect of H2O2 and 2-MT on the Chemical Mechanical Polishing of Cobalt Adhesion Layer in Acid Slurry