Abstract:Ni improves toughness in martensitic steels. However, the effect of Si on grain refining and toughness of martensitic steel for high-strength applications including armor grades has not been much studied, which can be also a cheaper alternative replacing Ni and without any micro-alloying addition. With this motivation, an initial laboratory study of a quenched and tempered high-Si steel (0.31C-1.25Si-1.19Mn-0.1Mo-0.29Ni) and low-Si steel (0.32C-0.49Si-0.61Mn-0.46Cr-0.1Mo-0.29Ni) showed that their full thickness Charpy impact energy at − 40 °C was 32 ± 3 and 15 ± 2 J, respectively, while their microstructures had maximum lath length 15 and 30 μm, respectively. Based on this, an industrial steel (0.30C-1.27Mn-1.23 Si-0.22 Mo-0.43Ni) was made through electric arc furnace—vacuum arc degassing—continuous casting route with low H2, O2 and N2 contents and hot rolled to 5.2-mm-thick coil, which finally processed to quenched and tempered plate. The air-cooled hot-rolled intermediate plate of 25 mm thickness revealed bainitic microstructure, while the slowly cooled hot-rolled coil sample showed banded microstructure consisting of proeutoctoid ferrite and pearlite. On the other hand, the ferrite bainitic microstructure was revealed when the steel was cooled at 1 °C/s through dilatometry using Gleeble 3500C. The bainitic microstructure at low cooling rate indicated high hardenability of this grade. The Ac3 transformation temperature determined by dilatometry was 850 °C. Based on this, oil quenching was carried out after heating at 895 °C for 7, 12 and 17 min, while low-temperature tempering was done at 250 °C for 60 min. The micrographs in these three heating conditions revealed fully martensitic microstructure consisting of fine laths. The hardness of plates varied in the range of 495-506 HBW after tempering at 250 °C for 1 h, while yield strength, tensile strength, percentage elongation and percentage of reduction in area varied in the range of 1500-1540, 1780-1820 MPa, 7.37-8.61 and 24.64-27.40, respectively. The Charpy impact energy of sub-size ½ thickness specimen varied closely in the range 11.5-13.8 J at − 40 °C and their corresponding fracture surfaces showed dimpled ductile rupture morphology that typically belonged to the upper shelf region of Charpy transition curve. The measured hardness, strength, elongation and Charpy energy are in accordance with the requirement of final product. Bright-field TEM image of the tempered steel showed the presence of fine laths and uniformly distributed needle-shaped fine carbides resembling ε-Fe2.4C.

High-Si-Content Quenched and Tempered Steel for High-Strength Application

Ultrahigh Ductility, High-Carbon Martensitic Steel

Mechanical Properties and Microstructures of A Novel Low Carbon High-Silicon Martensitic Steel

Development of Direct Quenching 800 MPa High Strength Low Alloy Steel Plate

Development of a Silicon Alloyed Hardened and Tempered Ultra High Strength Steel

Significant Improvement in Strength and Toughness of Nanoscale Precipitate–Strengthened Steel by Direct Quenching and Tempering Process

High strength-elongation product of Nb-microalloyed low-carbon steel by a novel quenching–partitioning–tempering process

Effect of Si Content on Microstructure and Properties of Low-Carbon Medium-Manganese Steel after Intercritical Heat Treatment

Competitive role of film-like austenite and transition carbides on hydrogen embrittlement resistance and impact toughness in bainite-containing quenched and partitioned steel

Microstructure and mechanical behavior of a novel Fe–Mn–C–Cr–Si high-manganese steel

325 Air-cooled Carbide Free Bainite-Martensitic Steel and Its Properties

Microstructure and mechanical properties of 18Mn3Si2CrMo steel subjected to austempering at different temperatures below M s

High strength-toughness combination of a low-carbon medium-manganese steel plate with laminated microstructure and retained austenite

Microstructure and mechanical properties of high-carbon Si-Al-rich steel by low-temperature austempering

Effect of Al Replacing Si on Mechanical Properties of High Carbon Q–P–T Martensitic Steels

Novel Ultrahigh-Strength Nanolath Martensitic Steel by Quenching–partitioning–tempering Process

Development of high strength plates with low yield ratio by the combination of TMCP and inter-critical quenching and tempering

Tailoring the Microstructure using Quenching and Partitioning Processing in a Commercial Mn-Si-Cr Spring Steel to Improve Tensile Properties

Effect of Intercritical Austenitizing Temperature during Quenching–Intercritical Quenching–Tempering Process on Toughness of 25Mn2Si2Cr Bainitic Steel

Microstructural evolution and mechanical properties of 60Si2CrVNb spring steel under quenching-tempering heat treatment process

MICRO-CRYSTAL STRUCTURE OF 57Fe15Cr25Ni0.32Mn0.96Si AUSTENITE STEEL AFTER 850°C-5H TEMPERATURE-QUENCHING TREATMENTS FOR HIGH TEMPERATURE MATERIAL APPLICATIONS