Abstract:Advanced high-strength steels (AHSS) have a wide range of applications in equipment safety and lightweight design, and enhancing the strength of AHSS to the ultra-high level of 2 GPa is currently a key focus. In this study, a new process of thermo-mechanical control process followed by direct quenching and partitioning (TMCP-DQP) was developed based on Fe-0.4C-1Mn-0.6Si (wt.%) low-alloy steel, and the effects of microstructure evolution on mechanical properties under TMCP-DQP process and conventional hot rolled quenched and tempered process (HR-QT) were comparatively studied. The results show that the TMCP-DQP process not only shortened the processing steps but also achieved outstanding comprehensive mechanical properties. The TMCP-DQP steel exhibited a tensile strength of 2.23 GPa, accompanied by 11.9% elongation and a Brinell hardness of 624 HBW, with an impact toughness of 28.5 J at −20 °C. In contrast, the HR-QT steel exhibited tensile strengths ranging from 2.16 GPa to 1.7 GPa and elongations between 5.2% and 12.2%. The microstructure of TMCP-DQP steel primarily consisted of lath martensite, containing thin-film retained austenite (RA), nanoscale rod-shaped carbides, and a minor number of nanoscale twins. The volume fraction of RA reached 7.7%, with an average carbon content of 7.1 at.% measured by three-dimensional atom probe tomography (3DAP). Compared with the HR-QT process, the TMCP-DQP process resulted in a finer microstructure, with a prior austenite grain (PAG) size of 11.91 μm, forming packets and blocks with widths of 5.12 μm and 1.63 μm. The TMCP-DQP process achieved the ultra-high strength of low-alloy steel through the synergistic effects of grain refinement, dislocation strengthening, and precipitation strengthening. The dynamic partitioning stage stabilized the RA through carbon enrichment, while the relaxation stage reduced a small portion of the dislocations generated by thermal deformation, and the self-tempering stage eliminated internal stresses, all guaranteeing considerable ductility and toughness. The TMCP-DQP process may offer a means for industries to streamline their manufacturing processes and provide a technological reference for producing 2.2 GPa grade AHSS.

Development of high strength plates with low yield ratio by the combination of TMCP and inter-critical quenching and tempering

Effects of Heat Treatment Process on Microstructure and Mechanical Properties for Extra-Thick High-Strength Steel Plate

Innovations in Thermo-mechanical Processing to Develop High Strength Steel Plates

Microstructural and Mechanical Properties Development During Quenching-Partitioning-Tempering Process of Nb-V-Ti Microalloyed Ultra-High Strength Steel

Variations in microstructure and mechanical properties along thickness direction in a heavy high strength low alloy steel plate

Synergetic Effects of Ferrite Content and Tempering Temperature on Mechanical Properties of a 960 MPa Grade HSLA Steel

New observations of the twinning effect and austenite stability in intercritical quenched and tempered steel with high strength

High strength-toughness combination of a low-carbon medium-manganese steel plate with laminated microstructure and retained austenite

Achieving 2.2 GPa Ultra-High Strength in Low-Alloy Steel Using a Direct Quenching and Partitioning Process

Study on Direct Quenching and Tempering Process of 1000mpa Grade Low Alloy High Strength Steel

Through a Controlled Quenching to Achieve a Good Combination of Mechanical Properties in Low‐Yield Ratio 900 MPa High‐Strength Low‐Alloy Steels

Influences of Quenching Temperature on the Microstructure Evolution and Strength−Toughness of a Novel Medium‐Carbon Ti−Mo‐Bearing Martensite Steel

Development of Ti–V–Mo Complex Microalloyed Hot-Rolled 900-MPa-Grade High-Strength Steel

Microstructure, Precipitation, and Strengthening Mechanism of a High‐Strength Q1100 Heavy Steel Plate via Niobium–Boron Microalloying Technology

Thermomechanical Processing for Improved Mechanical Properties of HT9 Steels

Effect of Intercritical Austenitizing Temperature during Quenching–Intercritical Quenching–Tempering Process on Toughness of 25Mn2Si2Cr Bainitic Steel

Study on Quenching and Tempering Process of 800 MPa High Strength Steel Plate

Evolution of Microstructures and Mechanical Properties During Solution Treatment of a Ti–V–Mo-containing High‑manganese Cryogenic Steel

Study on Microstructure and Mechanical Properties of TMCP-UFC-LT Treated Low Ni Steel

A Carbide-Free Bainite/martensite/austenite Triplex Steel with Enhanced Mechanical Properties Treated by a Novel Quenching–partitioning–tempering Process

The Fabrication of Ultrahigh-Strength Steel with a Nanolath Structure via Quenching-Partitioning-Tempering