Abstract:Advanced high-strength steels (AHSS) have a wide range of applications in equipment safety and lightweight design, and enhancing the strength of AHSS to the ultra-high level of 2 GPa is currently a key focus. In this study, a new process of thermo-mechanical control process followed by direct quenching and partitioning (TMCP-DQP) was developed based on Fe-0.4C-1Mn-0.6Si (wt.%) low-alloy steel, and the effects of microstructure evolution on mechanical properties under TMCP-DQP process and conventional hot rolled quenched and tempered process (HR-QT) were comparatively studied. The results show that the TMCP-DQP process not only shortened the processing steps but also achieved outstanding comprehensive mechanical properties. The TMCP-DQP steel exhibited a tensile strength of 2.23 GPa, accompanied by 11.9% elongation and a Brinell hardness of 624 HBW, with an impact toughness of 28.5 J at −20 °C. In contrast, the HR-QT steel exhibited tensile strengths ranging from 2.16 GPa to 1.7 GPa and elongations between 5.2% and 12.2%. The microstructure of TMCP-DQP steel primarily consisted of lath martensite, containing thin-film retained austenite (RA), nanoscale rod-shaped carbides, and a minor number of nanoscale twins. The volume fraction of RA reached 7.7%, with an average carbon content of 7.1 at.% measured by three-dimensional atom probe tomography (3DAP). Compared with the HR-QT process, the TMCP-DQP process resulted in a finer microstructure, with a prior austenite grain (PAG) size of 11.91 μm, forming packets and blocks with widths of 5.12 μm and 1.63 μm. The TMCP-DQP process achieved the ultra-high strength of low-alloy steel through the synergistic effects of grain refinement, dislocation strengthening, and precipitation strengthening. The dynamic partitioning stage stabilized the RA through carbon enrichment, while the relaxation stage reduced a small portion of the dislocations generated by thermal deformation, and the self-tempering stage eliminated internal stresses, all guaranteeing considerable ductility and toughness. The TMCP-DQP process may offer a means for industries to streamline their manufacturing processes and provide a technological reference for producing 2.2 GPa grade AHSS.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is: how to achieve an ultra - high strength of 2.2 GPa for low - alloy steel through the thermomechanical control process combined with direct quenching and partitioning treatment (TMCP - DQP), while maintaining excellent plasticity and toughness. Specifically, the research objectives of the paper include: 1. **Develop a new process**: Based on Fe - 0.4C - 1Mn - 0.6Si (mass fraction) low - alloy steel, develop a new method of direct quenching and partitioning treatment (TMCP - DQP) after a new thermomechanical control process. 2. **Improve steel performance**: Through this new process, make the low - alloy steel reach an ultra - high strength of 2.2 GPa while maintaining good ductility and toughness. 3. **Optimize the microstructure**: Study the influence of the TMCP - DQP process on the evolution of the steel microstructure and conduct a comparative analysis with the traditional hot - rolling quenching and tempering (HR - QT) process. 4. **Reveal the strengthening mechanism**: Explore the mechanism of the synergistic effects such as grain refinement, dislocation strengthening and precipitation strengthening in achieving the ultra - high strength of steel. The key issues mentioned in the paper also include: - Although the currently produced advanced high - strength steels (AHSS) through the DQP process have excellent mechanical properties, it is still a major challenge to exceed a tensile strength of 2 GPa. - There is still a lack of comprehensive research on the synergistic influence of TMCP technology and the dynamic partitioning treatment process on the mechanical properties of steel and the mechanism of microstructure evolution. Therefore, this paper aims to fill this research gap and provide a technical reference for the industrial production of AHSS at the 2.2 GPa level.

Achieving 2.2 GPa Ultra-High Strength in Low-Alloy Steel Using a Direct Quenching and Partitioning Process

Microstructure Features and Tensile Properties of a Recent Ultra-High-Strength Steel via Two-Step Quenching and Partitioning Process

The Fabrication of Ultrahigh-Strength Steel with a Nanolath Structure via Quenching-Partitioning-Tempering

Design of tough, ductile direct quenched and partitioned advanced high-strength steel with tailored silicon content

Effect of hot stamping and quenching & partitioning process on microstructure and mechanical properties of ultra-high strength steel

Study of Quenching and Partitioning (Q&P) and Ultrasonic Surface Rolling (USR) Process on Microstructure and Mechanical Property of a High-Strength Martensitic Steel

Dual Nanoprecipitation and Nanoscale Chemical Heterogeneity in a Secondary Hardening Steel for Ultrahigh Strength and Large Uniform Elongation

A novel microstructural design and heat treatment technique based on gradient control of carbon partitioning between austenite and martensite for high strength steels

Design of Tri-Phase Lamellar Architectures for Enhanced Ductility in Ultra-Strong Steel

A Carbide-Free Bainite/martensite/austenite Triplex Steel with Enhanced Mechanical Properties Treated by a Novel Quenching–partitioning–tempering Process

Achieving ultrahigh strength by tuning the hierarchical structure of low-carbon martensitic steel

Hot-Rolling and a Subsequent Direct-Quenching Process Enable Superior High-Cycle Fatigue Resistance in Ultra-High Strength Low Alloy Steels

Through a Controlled Quenching to Achieve a Good Combination of Mechanical Properties in Low‐Yield Ratio 900 MPa High‐Strength Low‐Alloy Steels

A cryogenic ultra-strong and ductile steel induced by stable nanoscale dual-phase structure

Development of high strength plates with low yield ratio by the combination of TMCP and inter-critical quenching and tempering

Process control maps to design an ultra-high strength-ductile steel

Microstructural and mechanical properties of ultra-high-strength dual-phase steel produced by ultra-fast cooling

Achieving 1.7 GPa Considerable Ductility High-Strength Low-Alloy Steel Using Hot-Rolling and Tempering Processes

Application of Intercritical Austenitizing in a Commercial CMnSi Steel as a Tool for Optimizing a One‐Step Quenching and Partitioning Cycle Aiming to Achieve a Third‐Generation Advanced High‐Strength Steel

Ultrahigh strength-ductile medium-Mn steel auto-parts combining warm stamping and quenching & partitioning

Tailoring hetero-grained austenite via a cyclic thermomechanical process for achieving ultrahigh strength-ductility in medium-Mn steel