Study of Quenching and Partitioning (Q&P) and Ultrasonic Surface Rolling (USR) Process on Microstructure and Mechanical Property of a High-Strength Martensitic Steel

Yi Hou,Chenfeng Duan,Xiaoqiang Li,Shengguan Qu
DOI: https://doi.org/10.3390/ma17112752
IF: 3.4
2024-06-06
Materials
Abstract:Steel with a combination of strength and plasticity is prevalently demanded for lightweight design and emission reductions in manufacturing. In this study, a high-strength Cr-Ni-Mo martensitic steel treated by quenching and partitioning (Q&P) and ultrasonic surface rolling (USR) processes was studied for both strength and plasticity enhancement. Specimens were austenitized at 850 °C and then quenched to 240 °C via cooling by water, oil, and normalization in quenching. This was followed by partitioning, in which two groups of specimens were heated to 370 °C and 350 °C for 45 min, respectively. At last, all the specimens were quenched to room temperature with the same methods of quenching. The highest tensile strength increased from 681.73 MPa to 1389.76 MPa when compared to as-received (AR) steel after the Q&P process. The USR process with a static force of 800 N further improved the tensile strength of specimens with high tensile strength after the Q&P process, which improved from 1389.76 MPa to 1586.62 MPa and the product's strength and elongation (PSE) increased from 15.76 GPa% to 15.9 GPa%, while the total elongation showed a mitigatory decrease from 11.34% to 10.02%. Tensile fractures were also studied and verified using a combination of strength and plasticity after a combined process of Q&P and USR.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to improve the mechanical properties of high - strength Cr - Ni - Mo martensitic steel through the quenching and partitioning (Q&P) and ultrasonic surface rolling (USR) processes, that is, to simultaneously increase its strength and plasticity. Specifically: 1. **Q&P Process**: - By controlling the quenching temperature and the partitioning temperature, the influence of different heat treatment parameters on the microstructure of the material is studied. - It aims to optimize the strength and plasticity of the material by forming bainite and thin - film retained austenite (RA). - The research found that the Q&P process can significantly increase the tensile strength of the material, from 681.73 MPa to 1389.76 MPa. 2. **USR Process**: - By performing USR treatment after the Q&P process, the surface strength of the material is further increased. - The USR process refines the grains through severe plastic deformation and forms a hardened layer, thereby enhancing the local hardness and tensile strength of the material. - The results show that after USR treatment, the tensile strength of the material is increased from 1389.76 MPa to 1586.62 MPa, and at the same time, the product of strength and elongation (PSE) is increased from 15.76 GPa% to 15.9 GPa%. 3. **Comprehensive Effect**: - The comprehensive effect after the combination of Q&P and USR processes is studied, and the influence of microstructure evolution and surface strengthening on the improvement of the mechanical properties of the material is verified. - Through tensile tests and fracture analysis, the improvement of these processes on the material properties is further confirmed. In conclusion, through systematic experiments and analysis, this paper explores how to effectively improve the comprehensive mechanical properties of high - strength Cr - Ni - Mo martensitic steel through the combination of Q&P and USR processes, especially the balance between strength and plasticity.