Abstract:Advanced high-strength steels (AHSS) have a wide range of applications in equipment safety and lightweight design, and enhancing the strength of AHSS to the ultra-high level of 2 GPa is currently a key focus. In this study, a new process of thermo-mechanical control process followed by direct quenching and partitioning (TMCP-DQP) was developed based on Fe-0.4C-1Mn-0.6Si (wt.%) low-alloy steel, and the effects of microstructure evolution on mechanical properties under TMCP-DQP process and conventional hot rolled quenched and tempered process (HR-QT) were comparatively studied. The results show that the TMCP-DQP process not only shortened the processing steps but also achieved outstanding comprehensive mechanical properties. The TMCP-DQP steel exhibited a tensile strength of 2.23 GPa, accompanied by 11.9% elongation and a Brinell hardness of 624 HBW, with an impact toughness of 28.5 J at −20 °C. In contrast, the HR-QT steel exhibited tensile strengths ranging from 2.16 GPa to 1.7 GPa and elongations between 5.2% and 12.2%. The microstructure of TMCP-DQP steel primarily consisted of lath martensite, containing thin-film retained austenite (RA), nanoscale rod-shaped carbides, and a minor number of nanoscale twins. The volume fraction of RA reached 7.7%, with an average carbon content of 7.1 at.% measured by three-dimensional atom probe tomography (3DAP). Compared with the HR-QT process, the TMCP-DQP process resulted in a finer microstructure, with a prior austenite grain (PAG) size of 11.91 μm, forming packets and blocks with widths of 5.12 μm and 1.63 μm. The TMCP-DQP process achieved the ultra-high strength of low-alloy steel through the synergistic effects of grain refinement, dislocation strengthening, and precipitation strengthening. The dynamic partitioning stage stabilized the RA through carbon enrichment, while the relaxation stage reduced a small portion of the dislocations generated by thermal deformation, and the self-tempering stage eliminated internal stresses, all guaranteeing considerable ductility and toughness. The TMCP-DQP process may offer a means for industries to streamline their manufacturing processes and provide a technological reference for producing 2.2 GPa grade AHSS.

Microstructure Features and Tensile Properties of a Recent Ultra-High-Strength Steel via Two-Step Quenching and Partitioning Process

Achieving 2.2 GPa Ultra-High Strength in Low-Alloy Steel Using a Direct Quenching and Partitioning Process

Microstructure and Mechanical Properties of an Ultrahigh-Strength 40SiMnNiCr Steel during the One-Step Quenching and Partitioning Process

Ultrahigh strength-ductility steel treated by a novel quenching–partitioning–tempering process

Room-Temperature Quenching and Partitioning Steel

Study of a Novel Ultra-High Strength Steel with Adequate Ductility and Toughness by Quenching-Partitioning-Tempering Process

Development of ultra high strength steel with high ductility by air cooling post single stage quench partitioning

Microstructure and Mechanical Properties of A Nb-Microalloyed Medium Carbon Steel Treated by Quenching-Partitioning Process

Novel Ultrahigh-Strength Nanolath Martensitic Steel by Quenching–partitioning–tempering Process

Mechanism exploration of an ultrahigh strength steel by quenching-partitioning-tempering process

Characterization of Microstructure and Mechanical Properties of a Nb-Microalloyed Steel after Quenching-Partitioning-Tempering Process

The Fabrication of Ultrahigh-Strength Steel with a Nanolath Structure via Quenching-Partitioning-Tempering

A novel microstructural design and heat treatment technique based on gradient control of carbon partitioning between austenite and martensite for high strength steels

Relationship Between Microstructure and Mechanical Properties of M50 Ultra-High Strength Steel Via Quenching-Partitioning-tempering Process

Tailoring Strength/ductility Combination in 2.5 Wt% Si-alloyed Middle Carbon Steel Produced by the Two-Step Q-P Treatment with a Prolonged Partitioning Stage

Microstructual Evolution of a Nb‐Microalloyed Advanced High Strength Steel Treated by Quenching‐Partitioning‐Tempering Process

Microstructural Evolution of Medium Carbon Steels during the Quenching and Partitioning Process

Study of Quenching and Partitioning (Q&P) and Ultrasonic Surface Rolling (USR) Process on Microstructure and Mechanical Property of a High-Strength Martensitic Steel

High strength-elongation product of Nb-microalloyed low-carbon steel by a novel quenching–partitioning–tempering process

Effect of Alloy Elements Partitioning Behavior on Retained Austenite and Mechanical Property in Low Carbon High Strength Steel

Ultrahigh Ductility, High-Carbon Martensitic Steel