Abstract:Silicon carbide (SiC) is an essential intermediate product formed during the smelting process of metallurgical-grade silicon (MG-Si), and its production efficiency is a key factor in determining the overall efficiency of MG-Si production. In this study, the effect of quartz-to-cristobalite transformation on SiC generation in MG-Si production and elucidated the differences in the reaction characteristics of quartz and cristobalite when they interacted with carbonaceous reductants. The experimental results indicated that the rate of direct carbothermal reduction of cristobalite was 1.45 times that of quartz. Moreover, the indirectly formed SiC layer in the cristobalite/C diffusion couple exhibited a thickness of 920.87 μm, which was 1.55 times that in the quartz/C diffusion couple. Both the reaction thermodynamic calculations and crystal transformation theory analysis revealed that the changes in the chemical energy and crystal structure of SiO 2 during the phase transformation process reduced the stability of cristobalite compared with quartz at high temperatures. Consequently, cristobalite reacted more easily with C at high temperatures to form SiC and SiO. The results of the study are highly significant for improving the reaction mechanism in the smelting process of MG-Si and enhancing the production efficiency of MG-Si.

Carbothermal Reduction of Quartz with Carbon from Natural Gas

Carbothermal Reduction Behavior of Micro-silica

Carbothermal Reduction of SiO2 Using Different Coal

Influences of Carbon Contents on the Products of Carbothermal Reduction-nitriding of Natural Quartz

Influence of Reaction Temperature and Zircon Addition on Product from Quartz by Carbothermal Reduction and Nitridation

A Study of the Effect of Quartz-to-Cristobalite Transformation on SiC Generation in Metallurgical-Grade Silicon Production

Effect of K 2 CO 3 as an Additive Agent on the Carbothermic Reduction Process of Silicon Production

Phase Behavior of Silica Brick Used in Carbothermal Reduction

Effect of Sintering Conditions on the Formation of SiC Nanomaterials in Carbothermal Reduction

Rapid Synthesis of SiC Powders by Spark Plasma-Assisted Carbothermal Reduction Reaction

Preparation of SiC Powders by Carbothermal Reduction with Bamboo Charcoal As Renewable Carbon Source

Experimental Study of White Carbon Black Prepared from Quartz

Preparation and Characterization of SiC Nanowires and Nanoparticles from Filter Paper by Sol–gel and Carbothermal Reduction Processing

Synchronistic Preparation of Fibre-Like Sic and Cubic-Zro2/Sic Composite from Zircon Via Carbothermal Reduction Process

Fabrication of ZrO2‐SiC Composites from Natural Zircon Ore by Carbothermal Reduction

Preparation of Biomorphic SiC Ceramic by Carbothermal Reduction of Oak Wood Charcoal

Synthesis and Characterization of Si/SiO2/SiC Composites Through Carbothermic Reduction of Rice Husk-based Silica

In-situ synthesis of SiC nanowires on biomass carbon materials derived from cherry stones

Carbothermic Reduction of Mullite at Elevated Temperature

Preparation Of Nanocrystalline Silicon Carbide Powders By Carbothermal Reduction

Theoretical and experimental study of the mechanism for preparation of SiC nanowires by carbothermal reduction