Abstract:In order to solve the problems (i.e. low infiltration efficiency, cracks, interface separation and poor mechanical properties) in the process of wood-derived C–SiC composites, the thermal modification of fir at low temperatures (300 °C ∼ 350 °C) combined with sol-gel infiltration was used to successfully produce biomorphic ceramics. The prepared materials were comprehensively characterized and exhibited improved interfacial bonding between C and SiC and mechanical properties. The weight gain per unit volume (0.123 g/cm 3 ) of SiO 2 gel in the fir thermally modified at 300 °C is 167.4%, higher than that (0.046 g/cm 3 ) of the unmodified fir. A well-bonded interface was formed between the SiO 2 gel and the pore wall of the fir thermally modified at 300 °C. With the increase of modification temperature from 300 °C to 350 °C, the distance between SiO 2 gel and the pore wall increases, and a gap (1–3 μm) is observed between SiO 2 gel and the pore wall of the fir carbonized at 600 °C. The C–SiC composites sintered at 1400 °C exhibited the highest compressive strength and bending strength of 40.8 ± 5.8 MPa and 11.7 ± 2.1 MPa, respectively, owing to the well-bonded interface between C of fir thermally modified at 300 °C and SiC. However, the composites sintered at 1600 °C for 120 min exhibited the lowest compressive strength and bending strength of 28.1 ± 13.4 MPa and 5.7 ± 1.6 MPa, respectively, which are 31.1% and 51.3% lower than those sintered at 1400 °C for 120 min, respectively. This might result from the porous structure formed by the excessive consumption of fir-derived carbon during the reaction between C and SiO 2 at 1600 °C for 120 min. Therefore, thermal modification in the preparation of biomorphic C–SiC composites can promote slurry infiltration and the formation of a well-bonded interface between C and SiC, thus improving the mechanical properties of the composites.

Preparation of Biomorphic SiC Ceramic by Carbothermal Reduction of Oak Wood Charcoal

Effect of Steam Activation on Development of Light Weight Biomorphic Porous SiC from Pine Wood Precursor

Preparation of Silicon Carbide Using Bamboo Charcoal As Carbon Source

Preparation of SiC Powders by Carbothermal Reduction with Bamboo Charcoal As Renewable Carbon Source

Preparation of biomorphic porous SiC and SiO2 ceramics by sol infiltration into biotemplate followed by controlled sintering

Preparation of Porous SiC Ceramic Using Bamboo Charcoal and Silica Sol As Pore-Forming Agents

Biomorphic Cellular Silicon Carbide Nanocrystal-Based Ceramics Derived from Wood for Use as Thermally Stable and Lightweight Structural Materials

Light-weight, wood-derived, biomorphic SiC ceramics by carbothermal reduction

Biomorphic Silicon/silicon Carbide Ceramics from Birch Powder

Optimized Vacuum/pressure Sol Impregnation Processing of Wood for the Synthesis of Silica/biocarbon Composite

In-situ synthesis of SiC nanowires on biomass carbon materials derived from cherry stones

Synthesis and Characterization of Si/SiO2/SiC Composites Through Carbothermic Reduction of Rice Husk-based Silica

Low-temperature thermally modified fir-derived biomorphic C–SiC composites prepared by sol-gel infiltration

Preparation and mechanical behaviors of multiscale SiC nanowires/carbon fiber reinforced silicon oxycarbide ceramic composites

Effect of Activator on Properties of SiC Porous Ceramics

Comparative Study of Biomorphic Silicon/Silicon Carbide Ceramic from Birch and Compressed Birch

Preparation and Properties of Porous Silicon Carbide Ceramics Through Coat-Mix and Composite Additives Process

Microstructure Evolution Process of Porous Silicon Carbide Ceramics Prepared Through Coat-Mix Method

Facile Fabrication of Nanofibrous Network Reinforced Hierarchical Structured Porous Si3N4-based Ceramics Based on Si-Si3N4 Binary Particle-Stabilized Foams

Fabrication and Properties of SiC/mullite Composite Porous Ceramics

High Temperature Structure Evolution of Macroporous SiOC Ceramics Prepared by a Sol–gel Method