Abstract:In order to solve the problems (i.e. low infiltration efficiency, cracks, interface separation and poor mechanical properties) in the process of wood-derived C–SiC composites, the thermal modification of fir at low temperatures (300 °C ∼ 350 °C) combined with sol-gel infiltration was used to successfully produce biomorphic ceramics. The prepared materials were comprehensively characterized and exhibited improved interfacial bonding between C and SiC and mechanical properties. The weight gain per unit volume (0.123 g/cm 3 ) of SiO 2 gel in the fir thermally modified at 300 °C is 167.4%, higher than that (0.046 g/cm 3 ) of the unmodified fir. A well-bonded interface was formed between the SiO 2 gel and the pore wall of the fir thermally modified at 300 °C. With the increase of modification temperature from 300 °C to 350 °C, the distance between SiO 2 gel and the pore wall increases, and a gap (1–3 μm) is observed between SiO 2 gel and the pore wall of the fir carbonized at 600 °C. The C–SiC composites sintered at 1400 °C exhibited the highest compressive strength and bending strength of 40.8 ± 5.8 MPa and 11.7 ± 2.1 MPa, respectively, owing to the well-bonded interface between C of fir thermally modified at 300 °C and SiC. However, the composites sintered at 1600 °C for 120 min exhibited the lowest compressive strength and bending strength of 28.1 ± 13.4 MPa and 5.7 ± 1.6 MPa, respectively, which are 31.1% and 51.3% lower than those sintered at 1400 °C for 120 min, respectively. This might result from the porous structure formed by the excessive consumption of fir-derived carbon during the reaction between C and SiO 2 at 1600 °C for 120 min. Therefore, thermal modification in the preparation of biomorphic C–SiC composites can promote slurry infiltration and the formation of a well-bonded interface between C and SiC, thus improving the mechanical properties of the composites.

Comparative Study of Biomorphic Silicon/Silicon Carbide Ceramic from Birch and Compressed Birch

Biomorphic Silicon/silicon Carbide Ceramics from Birch Powder

Effect of starting Si contents on the properties and structure of biomorphic SiC ceramics

Preparation of Biomorphic SiC/C Ceramics from Pine Wood Via Supercritical Ethanol Infiltration

Preparation of Biomorphic SiC Ceramic by Carbothermal Reduction of Oak Wood Charcoal

Biomorphic SiC Ceramics Prepared by Organic Template Method

Preparation and characterization of porous, biomorphic SiC ceramic with hybrid pore structure

Effect of Steam Activation on Development of Light Weight Biomorphic Porous SiC from Pine Wood Precursor

Optimized Vacuum/pressure Sol Impregnation Processing of Wood for the Synthesis of Silica/biocarbon Composite

Preparation of Porous Sic Ceramic with A Woodlike Microstructure by Sol-Gel and Carbothermal Reduction Processing

Effect of Holding Time on the Basic Properties of Biomorphic Sic Ceramic Derived from Beech Wood

Porous SiC Ceramic Prepared by Reactive Infiltration of Liquid Silicon into Woodceramics

Preparation of Macroporous SiC from Si and Wood Powder Using Infiltration-Reaction Process

Biomorphic Cellular Silicon Carbide Nanocrystal-Based Ceramics Derived from Wood for Use as Thermally Stable and Lightweight Structural Materials

Microstructure analysis of morph-genetic SiC/C ceramics from wood

Preparation of Biomorphic Sic-Ceramics by the Reactive Infiltration on of Si into Carbon Template Derived from Basswood

Preparation and Properties of Porous Microcellular SiC Ceramics by Reactive Infiltration of Si Vapor into Carbonized Basswood

PREPARATION OF POROUS SiC CERAMIC BY GASEOUS REACTIVE INFILTRATION METHOD

Low-temperature thermally modified fir-derived biomorphic C–SiC composites prepared by sol-gel infiltration

Improvement of Mechanical Property of Biomass-Derived Porous Carbon Material Through in Situ Growth of SiCnws and Glucose-Converted Pyrolysed Carbon

Mechanical Properties and Microstructure of Si/Sic Materials Derived from Native Wood