Abstract:A new woodceramics was developed by carbonizing phenolic resin–basswood powder composite under vacuum. Structural characterization of woodceramics was performed by scanning electron microscopy (SEM), X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FT-IR) techniques. The pyrolytic behaviors of basswood powder and phenolic resin were studied by thermogravimetric analysis (TGA). The effects of carbonization temperature and weight ratio of phenolic resin to basswood powder on the volume electrical resistivity, open porosity and bending strength of woodceramics were also investigated. Experimental results show that woodceramics has a topologically uniform interconnected porous network microstructure, and is typical non-graphitizable carbon containing CC bonds, COC bonds and CH structure. With increasing carbonization temperature, the (002) peak becomes stronger, the (002) interplanar spacing and volume electrical resistivity decrease, and the dimensions of carbonized wood powder decrease, while the space between carbonized basswood powders and the open porosity and bending strength of woodceramics increase. The increasing weight ratio of phenolic resin to basswood powder improves the forming ability of phenolic resin impregnated wood powders, and results in a more uniform microstructure, but there is a slight effect on the XRD pattern of woodceramics. The volume electrical resistivity and open porosity decrease, and the bending strength increases as the weight ratio of phenolic resin to wood powder increases.

Porous SiC Ceramic Prepared by Reactive Infiltration of Liquid Silicon into Woodceramics

PREPARATION OF MACROPOROUS SiC FROM WOODCERAMICS AND SILICON POWDER BY IN SITU REACTION-SINTERING PROCESS

Preparation of Macroporous SiC from Si and Wood Powder Using Infiltration-Reaction Process

PREPARATION OF POROUS SiC CERAMIC BY GASEOUS REACTIVE INFILTRATION METHOD

Preparation and Properties of Porous Microcellular SiC Ceramics by Reactive Infiltration of Si Vapor into Carbonized Basswood

FABRICATION OF SiC CERAMIC WITH OAK WOOD MICROSTRUCTURE BY REACTIVE INFILTRATION OF GASEOUS SILICON

Effect of Phenolic Resin on the Basic Properties of Woodceramics and Biomorphic SiC Ceramics

Porous SiC Ceramics Fabricated by Reactive Infiltration of Gaseous Silicon into Charcoal

Woodceramics Prepared from Basswood Powder and Phenolic Resin

Preparation of Biomorphic SiC/C Ceramics from Pine Wood Via Supercritical Ethanol Infiltration

Preparation and characterization of porous, biomorphic SiC ceramic with hybrid pore structure

Preparation of Porous Sic Ceramic with A Woodlike Microstructure by Sol-Gel and Carbothermal Reduction Processing

Preparation of Biomorphic SiC Ceramic by Carbothermal Reduction of Oak Wood Charcoal

Preparation of Biomorphic Sic-Ceramics by the Reactive Infiltration on of Si into Carbon Template Derived from Basswood

Microstructure analysis of morph-genetic SiC/C ceramics from wood

STUDY ON STRUCTURAL CHANGES DURING PREPARING WOODCERAMICS FROM PHENOLIC RESIN/BASSWOOD POWDER COMPOSITE

Mechanical Properties and Microstructure of Si/Sic Materials Derived from Native Wood

Two kinds of preparations for porous SiC ceramics

Biomorphic SiC Ceramics Prepared by Organic Template Method

Structure and basic properties of woodceramics made from phenolic resin–basswood powder composite

Microstructure Transmissibility in Preparing Sic Ceramics from Natural Wood