Abstract:The paper presents the influence of the temperature of the sintering process on the microstructure and selected properties of boron carbide/TiB2/SiC composites obtained in situ by spark plasma sintering (SPS). The homogeneous mixture of boron carbide and 5% vol. Ti5Si3 micropowders were used as the initial material. Spark plasma sintering was conducted at 1700 °C, 1800 °C, and 1900 °C for 10 min after the initial pressing at 35 MPa. The heating and cooling rate was 200 °C/min. The obtained boron carbide composites were subjected to density measurement, an analysis of the chemical and phase composition, microstructure examination, and dry friction-wear tests in ball-on-disc geometry using WC as a counterpart material. The phase compositions of the produced composites differed from the composition of the initial powder mixture. Instead of titanium silicide, two new phases appeared: TiB2 and SiC. The complete disappearance of Ti5Si3 was accompanied by a decrease in the boron carbide content of the stoichiometry formula B13C2 and an increase in the content of TiB2, while the SiC content was almost constant. The relative density of the obtained boron carbide composites, as well as their hardness and resistance to wear, increased with the sintering temperature and TiB2 content. Unfortunately, the reactions occurring during sintering did not allow us to obtain composites with high density and hardness. The relative density was 76–85.2% of the theoretical one, while the Vickers hardness was in the range of 4–12 GPa. The mechanism wear of boron carbide composites tested in friction contact with WC was abrasive. The volumetric wear rate (Wv) of composites decreased with increasing sintering temperature and TiB2 content. The average value of coefficient of friction (CoF) was in the range of 0.54–0.61, i.e., it did not differ significantly from the value for B4C sinters.

Cold sintering preparation of B 4 C@SiO 2 /20BP ceramic matrix composite and its dry tribological properties

Preparation of B4Cp/Al Composites via Selective Laser Melting and Their Tribological Properties

Microstructures and mechanical properties of B4C‐SiC and B4C‐SiC‐TiB2 ceramic composites fabricated by hot pressing

Dry sliding friction and wear properties of B4C particulate-reinforced Al-5083 matrix composites

Reaction mechanism and friction behavior of an in-situ Ti/B4C composite synthesized by spark plasma sintering

Sn-containing Si3N4-based composites for adaptive excellent friction and wear in a wide temperature range

Study on the tribological properties of MoB/Cu laminated composite materials fabricated by hot-pressing process

B4C-SiC skeleton reinforced graphite composites with excellent mechanical properties

Enhancement mechanical properties of in-situ preparated B4C-based composites with small amount of (Ti3SiC2+Si)

Effect of grain size on tribological behavior of hot‐pressed boron carbide sliding against alumina balls

High-performance B4C matrix composites fabricated from the B4C–Si–CeO2 system via reactive hot pressing

Processing and mechanical properties of B4C-SiCw ceramics densified by spark plasma sintering

The Microstructure, Mechanical, and Friction-Wear Properties of Boron Carbide-Based Composites with TiB2 and SiC Formed In Situ by Reactive Spark Plasma Sintering

Effect of fiber orientation on tribological properties of fiber reinforced C/C‐SiC composites mated with ceramic ball

Influence of Silicon Addition on the Sintering Behavior and Mechanical Properties of Boron Carbide by SPS Process

Tribological Behavior of Liquid Phase Sintered SiC Ceramics Under Dry Condition

In situ preparation of a SiC–TiB2 composite and its wear fracture mechanism at high temperatures

Through-thickness particle distribution, microstructure evolution and tribological performance of B 4 C/BN-AA6061 composite via friction stir processing

Micro-Tribological Behavior of Boron Carbide Self-Mated Pairs

Mechanical and tribological properties of hot-pressed h-BN/Si3N4 ceramic composites

Tribological Properties of EP Composites Reinforced with Short Glass Fiber, Graphite, PTFE and B4C Under Oil Lubrication