Low temperature synthesis and densification of (Ti,V,Nb,Ta,Mo)(C,N) high-entropy carbonitride ceramics
Chong Jing,Sheng-Jian Zhou,Wen Zhang,Zhao-Ying Ding,Zhan-Guo Liu,Yu-Jin Wang,Jia-Hu Ouyang
DOI: https://doi.org/10.1016/j.jallcom.2022.167095
IF: 6.2
2022-09-11
Journal of Alloys and Compounds
Abstract:The single-phase (Ti 0.2 V 0.2 Nb 0.2 Ta 0.2 Mo 0.2 )(C 0.9 N 0.1 ) high-entropy carbonitride powder with an average particle size of 203 nm and a low oxygen content of 0.2915 wt% was synthesized by the carbothermal reduction-nitridation method at 1600 °C for 4 h. Subsequently, (Ti,V,Nb,Ta,Mo)(C,N) high-entropy carbonitride ceramics were prepared by hot pressing at temperatures of 1600 °C to 1900 °C. Increasing the sintering temperature is conducive to the uniform distribution of metallic elements, however, the hardness of high-entropy carbonitride ceramics is also reduced. (Ti,V,Nb,Ta,Mo)(C,N) ceramic hot-pressed at 1600 °C for 1 h has a relative density of 99.8%, an average grain size of 0.37 ± 0.08 μm, nanoindentation hardness of 32.4 ± 0.9 GPa, Vickers' hardness of 24.0 ± 0.7 GPa at 9.8 N and fracture toughness of 4.87 ± 0.25 MPa·m 1/2 , which is comparable to those of high-entropy carbides and nitrides. In this study, a novel and convenient method for the preparation of (Ti,V,Nb,Ta,Mo)(C,N) high-entropy carbonitride ceramics was established.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering