Abstract:Objectives. The aim of this study was to evaluate the corrosion behavior and cytocompatibility of a Co–Cr and two Ni–Cr dental alloys before and after the pretreatment with a biological saline solution. Methods. A commercial cobalt–chromium (Co–Cr) and two nickel–chromium (Ni–Cr) dental alloys [beryllium (Be)-free and Be-containing] were selected and pretreated with a biological saline solution containing 3% bovine serum albumin (BSA) for 72 h. Before and after the pretreatment, alloy specimens were examined for surface element compositions using X-ray photoelectron spectroscopy (XPS). Corrosion behavior and metal ion release were measured by electrochemical corrosion and immersion tests in artificial saliva respectively. The released metal ions in the exposed biological saline solution were also detected after the pretreatment for 72 h. 3T3 fibroblasts were cultured and exposed to specimens. After 4 hours of incubation, cell morphology and spreading were observed under a laser scanning confocal microscope. Cell proliferations were evaluated using CCK-8 assay after culturing for 1, 3 and 6 days. Results. After the pretreatment with a biological saline solution, the corrosion potential (Ecorr) and breakdown potential (Ebr) of the three dental alloys increased significantly, which corresponded with evident decreases of Co, Ni and Be levels on the alloy surfaces measured by XPS. The corrosion current (Icorr) and the polarization resistance (Rp) of the three alloys were not significantly affected by the pretreatment, corresponding to the slight reductions of Cr, molybdenum (Mo) and oxygen (O) levels on the surfaces of alloys except the Be-containing alloy. For the three alloys, the pretreatment obviously decreased the metal ions release in artificial saliva. There were a large amount of metal ions, including Co, Ni and Be ions, released from the alloys in the exposed biological saline solution after the pretreatment for 72 h. The results of in vitro study demonstrated that the pretreatment up-regulated cell spreading and proliferation on the three metallic substrates. Conclusions. The pretreatment with a biological saline solution optimized the surface elemental compositions of a Co–Cr and two Ni–Cr dental alloys by removing more labile metal elements from the alloy surfaces in form of cations. The corrosion susceptibility and metal ion release of the three dental alloys decreased significantly after the pretreatment, which led to improvements of their cytocompatibility.

Effect of pre-annealing temperature on electrochemical corrosion performance of the Au50Ag25Pd25 alloy in human artificial saliva

An electrochemical study on corrosion behavior of three alloys in artificial saliva with different pH

The Effect on the Corrosion Resistance of Ti Alloy in the Artificial Saliva with Different pH Value

Electrochemical impedance spectroscopy study of corrosion characteristics of palladium-silver dental alloys

The developments in corrosion and protection of dental alloys

[Microbial Corrosion of Dental Alloy].

Effects of pre-annealing process on microstructure and properties of the Cu-12%Ag composite wire

Influence of finishing on the electrochemical properties of dental alloys.

Comparison of Two Different Electro Polish Temperature on Cobalt Ion Release of Chromium Cobalt Alloy in Artificial Saliva with Atomic Absorption Spectrophotometry

Effect of Ag on the Corrosion Behavior of Ti–Ag Alloys in Artificial Saliva Solutions

Corrosion Behavior of Ti–5Ag Alloy with and Without Thermal Oxidation in Artificial Saliva Solution

Amorphous alloys resistant to corrosion in artificial saliva solution

Corrosion behavior of newly developed Ti-Ag-Fe dental alloys in neutral saline solution

Corrosion behavior and cytocompatibility of a Co–Cr and two Ni–Cr dental alloys before and after the pretreatment with a biological saline solution

Use of Electropolishing in Orthodontic Appliances: An Option to Reduce the Risk of Metal Hypersensitivity

The electrochemical behavior and surface analysis of Ti<sub>49.6</sub>Ni<sub>45.1</sub>Cu<sub>5</sub>Cr<sub>0.3</sub>alloy for orthodontic usage

Ni–Cr dental alloys - porcelain firing impact on corrosion properties and surface characteristics.

The Electrochemical Behavior And Surface Analysis Of Ti49.6ni45.1cu5cr0.3 Alloy For Orthodontic Usage

In-Vitro Assessment of the Corrosion Potential of an Oral Strain of Sulfate-Reducing Bacteria on Metallic Orthodontic Materials

Tin Silver Alloy as a Biomaterial: Corrosion Characteristics and Cellular Behavior

Effect of sanitizing solutions on cobalt chromium alloys for dental prostheses: A systematic review of in vitro studies