Abstract:In this research, Ag element was selected as an antibacterial agent to develop an antibacterial Ti–Ag alloy by a powder metallurgy. The microstructure, phase constitution, mechanical properties, corrosion resistance and antibacterial properties of the Ti–Ag sintered alloys have been systematically studied by X-ray diffraction (XRD), scanning electron microscope (SEM), compressive test, electrochemical measurements and antibacterial test. The effects of the Ag powder size and the Ag content on the antibacterial property and mechanical property as well as the anticorrosion property have been investigated. The microstructure results have shown that Ti–Ag phase, residual pure Ag and Ti were the mainly phases in Ti–Ag(S75) sintered alloy while Ti2Ag was synthesized in Ti–Ag(S10) sintered alloy. The mechanical test indicated that Ti–Ag sintered alloy showed a much higher hardness and the compressive yield strength than cp-Ti but the mechanical properties were slightly reduced with the increase of Ag content. Electrochemical results showed that Ag powder size had a significant effect on the corrosion resistance of Ti–Ag sintered alloy. Ag content increased the corrosion resistance in a dose dependent way under a homogeneous microstructure. Antibacterial tests have demonstrated that antibacterial Ti–Ag alloy was successfully prepared. It was also shown that the Ag powder particle size and the Ag content influenced the antibacterial activity seriously. The reduction in the Ag powder size was benefit to the improvement in the antibacterial property and the Ag content has to be at least 3wt.% in order to obtain a strong and stable antibacterial activity against Staphylococcus aureus bacteria. The bacterial mechanism was thought to be related to the Ti2Ag and its distribution.

Effect of Ag on the Corrosion Behavior of Ti–Ag Alloys in Artificial Saliva Solutions

The Effect on the Corrosion Resistance of Ti Alloy in the Artificial Saliva with Different pH Value

Corrosion Behavior of Ti–5Ag Alloy with and Without Thermal Oxidation in Artificial Saliva Solution

An electrochemical study on corrosion behavior of three alloys in artificial saliva with different pH

Effect of Ph Value and Fluoride Ions on Corrosion Resistance of Pure Ti and Ni-Cr-Ti Alloy in Artificial Saliva

Research development of corrosion of titanium in the oral bioenvironment

Corrosion behavior of newly developed Ti-Ag-Fe dental alloys in neutral saline solution

Comparative Study on the Corrosion Behavior of Ti–Nb and TMA Alloys for Dental Application in Various Artificial Solutions

Surface Characterization and Cell Response of Binary Ti-Ag Alloys with CP Ti As Material Control

Effects of Artificial Saliva with Albumen on Corrosion Behavior of Titanium

Adsorption of Candida albicans on Ti-6Al-4V surface and its corrosion effects in artificial saliva

The Physical and Antibacterial Properties of Argentine-Doped TiO2 Film on Stainless Steel Substrate

Corrosion Resistance of Dental Alloys in Artificial Saliva

Effect of Anodic Oxidation Pulse Voltage on Antibacterial Properties and Biocompatibility of Ti-Ag Alloy

Corrosion of Dental Alloys in Artificial Saliva with Streptococcus Mutans.

Development of Ti-Ag-Fe ternary titanium alloy for dental application.

The electrochemical behavior and surface analysis of Ti<sub>49.6</sub>Ni<sub>45.1</sub>Cu<sub>5</sub>Cr<sub>0.3</sub>alloy for orthodontic usage

The Electrochemical Behavior And Surface Analysis Of Ti49.6ni45.1cu5cr0.3 Alloy For Orthodontic Usage

Microstructure, Mechanical Properties, Bio-Corrosion Properties and Antibacterial Properties of Ti-Ag Sintered Alloys

Effect of Nano/micro-Ag Compound Particles on the Bio-Corrosion, Antibacterial Properties and Cell Biocompatibility of Ti-Ag Alloys.

Effect of fluoride on the corrosion behavior of Ti and Ti6Al4V dental implants coupled with different superstructures.