Abstract:Statement of problem: One of the main challenges facing dental implant success is peri-implantitis. Recent evidence indicates that titanium (Ti) corrosion products and undetected-residual cement are potential risk factors for peri-implantitis. The literature on the impact of various types of dental cement on Ti corrosion is very limited. Purpose: This study aimed to determine the influence of dental cement on Ti corrosion as a function of cement amount and type. Materials and methods: Thirty commercially pure Ti grade 4 discs (19 × 7mm) were polished to mirror-shine (Ra ≈ 40 nm). Samples were divided into 10 groups (n = 3) as a cement type and amount function. The groups were no-cement as control, TempBond NE (TB3mm, TB5mm, and TB8mm), FujiCEM-II (FC3mm, FC5mm, and FC8mm), and Panavia-F-2.0 (PC3mm, PC5mm, and PC8mm). Tafel's method estimated corrosion rate (icorr) and corresponding potential (Ecorr) from potentiodynamic curves. Electrochemical Impedance Spectroscopy (EIS) data was utilized to obtain Nyquist and Bode plots. An equivalent electrical circuit estimated polarization resistance (Rp) and double-layer capacitance (Cdl). Inductively coupled plasma mass spectrometry (ICP-MS) analysis was conducted to analyze the electrolyte solution after corrosion. pH measurements of the electrolyte were recorded before and after corrosion tests. Finally, the corroded surface was characterized by a 3D white-light microscope and scanning electron microscope. Statistical analysis was conducted using either one-way ANOVA followed by Tukey's Post Hoc test or Kruskal-Wallis followed by Dunn's test based on data distribution. Results: Based on cement amount, FC and PC significantly increased icorr in higher amounts (FC8mm-icorr = 8.22 × 10-8A/cm2, PC8mm-icorr = 5.61 × 10-8A/cm2) compared to control (3.35 × 10-8A/cm2). In contrast, TB3mm decreased icorr significantly compared to the control. As a function of cement type, FC increased icorr the most. EIS data agrees with these observations. Finally, corroded surfaces had higher surface roughness (Ra) compared to non-corroded surfaces. Conclusion: The study indicated that cement types FC and PC led to increased Ti-corrosion as a function of a higher amount. Hence, the implant stability could be impacted by the selection, excessive cement, and a potentially increased risk of peri-implantitis.

Effect of fluoride on the corrosion behavior of Ti and Ti6Al4V dental implants coupled with different superstructures.

Influence of Fluoride-Containing Acidic Artificial Saliva on the Mechanical Properties of Nickel-Titanium Orthodontics Wires.

Research development of corrosion of titanium in the oral bioenvironment

The developments in corrosion and protection of dental alloys

Corrosion behavior of Ti-39Nb alloy for dentistry

Corrosion resistance studies of copper and magnesium-doped fluorohydroxyapatite coatings on titanium biomaterial

INFLUENCE OF FLUORIDE ION CONCENTRATIONS ON THE CORROSION BEHAVIOR OF Ta2N NANOCRYSTALLINE COATING FOR DENTAL IMPLANT APPLICATIONS

Comparative Study on the Corrosion Behavior of Ti–Nb and TMA Alloys for Dental Application in Various Artificial Solutions

Effect of Fluoride-Ion Implantation on the Biocompatibility of Titanium for Dental Applications

Effect of Ph Value and Fluoride Ions on Corrosion Resistance of Pure Ti and Ni-Cr-Ti Alloy in Artificial Saliva

Exploring the effect of chlorhexidine concentration on the biocorrosion behavior of Ti6Al4V for dental implants

Corrosion resistance of stainless steel, nickel-titanium, titanium molybdenum alloy, and ion-implanted titanium molybdenum alloy archwires in acidic fluoride-containing artificial saliva: An in vitro study

Effect of PMMA sealing treatment on the corrosion behavior of plasma electrolytic oxidized titanium dental implants in fluoride-containing saliva solution

Tribocorrosion under galvanic interaction of Ti6Al4V and NiCr implant alloys

The effect of three dental cement types on the corrosion of dental implant surfaces

Enhancing the In Vitro Tribocorrosion Resistance of Titanium Alloy by Precipitation of Nano-Ti2Cu Phases

Ti-Ions and/or Particles in Saliva Potentially Aggravate Dental Implant Corrosion

Biological and Biomechanical Behavior of Titanium Implants with Fluoridated Hydroxyapatite Coatings

Electrochemical Behavior of Ti6Al4V Alloy Used in Dental Implants Immersed in Streptococcus gordonii and Fusobacterium nucleatum Solutions

In vitro corrosion behavior of coated Ti6Al4V with TiO2, ZrO2, and TiO2/ZrO2 mixed nanofilms using atomic layer deposition for dental implants

Microstructural evolution and corrosion behavior of Ti–6Al–4V alloy fabricated by laser metal deposition for dental applications