Abstract:W-Ni alloy has been an important engineering material in military, nuclear industry and many other fields because of its excellent properties such as high strength and superior heat/corrosion/oxidation resistances. As a mainstream additive manufacturing technology based on powder-bed-fusion principle, selective laser melting (SLM) is suitable for the rapid fabrication of very complex W-Ni alloy components. However, researches on the powder densification behavior and microstructure formation mechanism of SLM W-Ni alloy are not thorough enough. In this work, a series of W-xNi (x = 16, 23, 30 wt.%) binary alloy samples were fabricated by SLM, using W/Ni mixed powders as the raw materials. The densification behaviors of the W/Ni mixed powders and the microstructure formation mechanisms of the different SLM W-Ni samples were studied. The results showed that when the W/Ni mixed powder bed was scanned by the laser, Ni powders with a relatively lower melting point would melt completely whereas W powders with a relatively higher melting point would rearrange themselves in the liquid Ni and only part of them could be dissolved into the liquid Ni. As the initial content of Ni powders increased, the rearrangement and dissolution of W powders proceed more sufficiently, thus leading to the improvement in densification degree. The relative densities of the W-16Ni, W-23Ni and W-30Ni SLM samples are 92.87 ± 0.67%, 98.66 ± 0.26% and 99.67 ± 0.18%, respectively. During the solidification processes of W-Ni molten pools, the precipitation of W grains from liquid Ni, the transformation of liquid Ni to γ-Ni solid solution and the precipitation of Ni2W from γ-Ni solid solution would occur in sequence. For the W-16Ni and W-23Ni samples, the grain morphology of the W precipitations is dendritic. For the W-30Ni samples, the W precipitations are globular. As a result of the unique melting- solidification behaviors, all the SLM samples possessed a tri-modal microstructure composed of unmelted W particles, dendritic/globular W grains, and γ-Ni solid solution with Ni2W intragranular precipitation. The average microhardness of the SLM W-Ni alloy samples decreased with the increase of Ni content, which could be explained by the variation in defect and microstructure features.

Eco-Friendly Material Extrusion 3D Printing for Fabricating W-Ni-Fe Lattices with Improved Compressive Resistance

Damping Behavior of 3d Woven Metallic Lattice Materials

Fabrication and Characterization of Tungsten Heavy Alloys with High W Content by Powder Metallurgy

Mechanical Properties of a Novel Tungsten Fiber-Reinforced Tungsten Composite Prepared Through Powder Extrusion Printing and High-Pressure High-Temperature Sintering

Laser powder bed fusion of a novel nano-modified tungsten alloy with refined microstructure and enhanced strength

The simultaneous improvement of strength and ductility of the 93W-4.6Ni-2.4Fe prepared by additive manufacturing via optimizing sintering post-treatment

Laser powder bed fusion of a tungsten-nickel-ferrum alloy via in-situ alloying: Densification, microstructure, and mechanical properties

Optimization of Isotactic Polypropylene Nanocomposite Content of Tungsten Carbide for Material Extrusion 3D Printing

Alloying Effects on the Microstructure and Properties of Laser Additively Manufactured Tungsten Materials

An Al-Al interpenetrating-phase composite by 3D printing and hot extrusion

Microstructure and mechanical properties of liquid–phase sintered W@NiFe composite powders

Dense Pure Tungsten Fabricated by Selective Laser Melting

Effects of laser printing parameters on molten pool formation, microstructure evolution and mechanical properties of laser directed energy deposition of difficult-to-process tungsten heavy-alloy

Powder densification behavior and microstructure formation mechanism of W-Ni alloy processed by selective laser melting

A defect-resistant Co-Ni superalloy for 3D printing

3D Printing of Continuous Fiber Reinforced Low Melting Point Alloy Matrix Composites: Mechanical Properties and Microstructures

Fabrication and characterization of W/Cu/Ni-based high specific gravity alloy with Zr and Ti combined addition

Development and Characterization of a Novel Fine-Grained W–Ni–Mn–Mo Alloys with La2O3 Addition Prepared Via Low-Temperature Sintering

Superior compressive properties of 3D printed plate lattice mechanical metamaterials

Simulation and Experimental Investigation on Additive Manufacturing of Highly Dense Pure Tungsten by Laser Powder Bed Fusion

A novel dissolution-precipitation mechanism during liquid phase sintering and its strengthening effects in W-Ni-Fe alloys with low W contents