Finite Element Analysis on Stress Field of Dissimilar Welded Joints under Deep Load Changing

Jie Liu,Chang Che,Feng Liu,Jianming Yu,Yong Xiang

DOI: https://doi.org/10.1109/aiars63200.2024.00047

2024-01-01

Abstract:In order to cope with the impact of the development of new energy power generation technology and study the safety state of thermal power units under low load or deep load changing conditions. In this paper, a two-dimensional finite element model is established by using large-scale simulation software COMSOL Multiphysics to study the stress field distribution of T91/TP347H dissimilar welded joints commonly used in power station boilers under load changing conditions. The results show that, the stress gradually tends to be stable with the increase of cycle times in the simulation of deep load changing with cyclic fluctuation at a set temperature of 500-625°C and internal pressure of 15-25MPa. At the 200th cycle, the maximum stress appears at the innermost of the TP347 H side fusion line at the load trough, reaching 275.45MPa. The maximum stress value appears at the interface between the base metal and the weld, and the stress is distributed along the interface. Near the inner side of the welded joint, the stress on the TP347H side fusion line is slightly larger than that on the T91 side fusion line. Near the outside of the welded joint, the tensile stress from the heat affected zone on the T91 side to the T91 base metal side is greater than that on the TP347H side. After 200 cycles of deep load changing simulation, the tensile stress at each position of the welded joint varies to varying degrees. Each position of the welded joint undergoes a process of stress from small to large at the peak of the load; during the load trough, it experienced a process from large to small; as the number of cycles increases, the stress at the peak of the load gradually increases, and the stress at the trough of the load gradually decreases, reaching a relatively stable state after 50 cycles.