Abstract:The selective growth of semiconducting single-walled carbon nanotubes (s-SWCNTs) is of great importance in many high-end applications represented by nanoelectronics. Here, we developed a general approach to grow horizontally aligned s-SWCNT arrays on stable temperature (ST)-cut quartz with bimetallic catalysts using carbon monoxide (CO) as both catalyst reductant and single component carbon feedstock under atmospheric pressure. The disproportionation of CO produces not only carbon species for SWCNT growth but also CO 2 , which could act as an in-situ etchant to remove both amorphous carbon and metallic tubes. The employment of bimetallic catalyst and quartz substrate facilitates the selective etching by narrowing the diameter distribution of as-grown SWCNT arrays. At the optimized conditions, we realized the selective growth of horizontally aligned s-SWCNT arrays with the content above 97% using CoCu catalysts, confirmed by Raman characterization and electrical measurements of the fabricated field effect transistor devices. This CO-based process in selective growth of s-SWCNTs has demonstrated its feasibility and universality by the broad growth window and applicability for other bimetallic catalysts, such as FeCu and CoMn. It possesses a practical potential in obtaining semiconducting channel materials for the scalable fabrication of CNT-based devices.

Chemical Vapor Depositions of Single-Walled Carbon Nanotubes Catalyzed by Uniform Fe(2)o(3) Nanoclusters Synthesized Using Diblock Copolymer Micelles.

Thin-Film Metal Catalyst For The Production Of Multi-Wall And Single-Wall Carbon Nanotubes

Influence of Cerium Metal As Catalyst on the Growth and Structure of Single-Walled Carbon Nanotubes

Growth of Single-Walled Carbon Nanotubes from Discrete Catalytic Nanoparticles of Various Sizes

Selective growth of semiconducting single-walled carbon nanotubes solely from carbon monoxide

Catalyst Design Using Nanoporous Iron for the Chemical Vapor Deposition Synthesis of Single-Walled Carbon Nanotubes

How Catalysts Affect the Growth of Single-Walled Carbon Nanotubes on Substrates

Narrow-chirality distributed single-walled carbon nanotube synthesized from oxide promoted Fe–SiC catalyst

Carbon fiber-promoted activation of catalyst for efficient growth of single-walled carbon nanotubes

Discrete Growth of Single-walled Carbon Nanotubes on Surfaces

CVD Growth of Carbon Nanotube Forest with Selective Wall-Number from Fe–Cu Catalyst

Revisiting behaviour of monometallic catalysts in chemical vapour deposition synthesis of single-walled carbon nanotubes

Microstructure Control of Fe Catalyst Films for the Growth of Multiwalled Carbon Nanotube Arrays

Controlled Growth of Fe Catalyst Film for Synthesis of Vertically Aligned Carbon Nanotubes by Glancing Angle Deposition

Bimetallic Catalysts for the Efficient Growth of SWNTs on Surfaces

Subnanometer Single-Walled Carbon Nanotube Growth from Fe-Containing Layered Double Hydroxides

Buliding microstructures of organized carbon nanotubes by chemical vapor deposition

Synthesis of uniformly distributed carbon nanotubes on a large area of Si substrates by thermal chemical vapor deposition

Growth of multi-walled carbon nanotubes on Si substrate with Fe3O4/DR film as catalyst precursors

Modulating the Diameter of Carbon Nanotubes in Array Form Via Floating Catalyst Chemical Vapor Deposition

Growth of High Quality, High Density Single-Walled Carbon Nanotube Forests on Copper Foils