Digital Light Processing of High-Strength Si3N4 Ceramics: Role of Particle Grading on Slurries Curing and Mechanical Properties

Jie Zhao,Wei Chu,Tao Song,Lunan Bi,Jia Liu,Zhuoqun Han,Yang Wang,Qingxuan Zhou,Ling Li

DOI: https://doi.org/10.1016/j.ceramint.2024.03.375

IF: 5.532

2024-01-01

Ceramics International

Abstract:Digital Light Processing (DLP) technology can achieve high-precision and high-efficiency molding of complex and irregularly shaped ceramic components. However, silicon nitride ceramics have high light absorption and large refractive index, leading to poor slurry curable performance and difficulty in molding. This study concentrates on the particle gradation of silicon nitride powder, investigating how varying proportions affect slurry rheology properties, curing properties, and the performance of the sintered body. When the ratio of fine/coarse powder was 7:3, the silicon nitride slurry with a solid content of 45 vol% had a viscosity of 5.4 Pa & sdot; s at a shear rate of 30 s -1 , a solidification thickness of 42 mu m (288 mJ/cm 2 ). The sintered body obtained the flexural strength of 679 MPa, with increases of 26.92% compared to the single coarse powder sample. Additionally, a complex shaped silicon nitride impeller suitable for high-temperature melt transport was successfully fabricated using DLP technology.