Abstract:The rod-like Cr(3)C(2 )micro-whiskers were successfully synthesized from chromic oxide and blank carbon as reaction sources and halide salts and nickel as catalysts by using a carbothermal reduction method assisted with high energy milling and liquid phase catalysis. The optimal preparing condition was to calcine the mixture of Cr2O3:C:NaCl:KCl:Ni = 1:8:0.4:0.4:0.3 (mole ratio) at 1300 degrees C for 2h without other post-treatments. The growth of Cr3C2 micro-whiskers was based on S-L-S mechanism that the brief reaction process of Cr2O3+C -> Cr7C3 -> Cr3C2 occurred in molten catalyst liquids. Besides, the deficiency of carbon led to the generation of Cr7C3 particles, and its excess could induce the formation of coral clusters. The obtained Cr3C2 whiskers were not oxidized in air atmosphere at temperature lower than 1000 degrees C, and a thin Cr2O3 coating which prevented further oxidation gradually formed on the outside of whiskers from 1000 to 1200 degrees C. In addition, the bonding strength of heat resistant adhesive was increased by 16-28% from 500 to 1500 degrees C after adding Cr3C2 whiskers, which was mainly attributed to the pull-out mechanism, whereas the added carbon fibers were completely oxidized and left many sags in adhesive structure, thus severely decreasing the strength. Molecular dynamics simulations with the tersoff forcefield were carried out to facilitate fundamental understanding of the micro-whiskers growing in preferred directions. Combined with theoretical and experimental studies, this work significantly expands the design space and motivates future efforts in exploring the emerging applications of the mechanical properties of Cr3C2 whiskers in severe occasions.

Preparation and Growth Mechanism of Tungsten Whiskers Fabricated by Oxidation-Reduction Method

Preparation of ZrO 2 whiskers through high pressure and high temperature method

Growth of single-crystal W whiskers during humid H2/N2 reduction of Ni, Fe–Ni, and Co–Ni doped tungsten oxide

Preparation and Growth Mechanism of Molybdenum Trioxide Whisker

Preparation and Growth Mechanism of TaCx Whiskers

A Study on the In-Situ Growth of Highly Oriented Zno Whisker

Structure and Field‐Emission Properties of Sub‐Micrometer‐Sized Tungsten‐Whisker Arrays Fabricated by Vapor Deposition

In-Situ Growth of ZnO Whiskers on Ti2ZnC MAX Phases

W18O49 Nanowhiskers Decorating SiO2 Nanofibers: Lessons from in-situ SEM/TEM Growth to Large Scale Synthesis and Fundamental Structural Understanding

Simple Approaches To Quality Large-Scale Tungsten Oxide Nanoneedles

Preparation of Well-Aligned ZnO Whiskers on Glass Substrate by Atmospheric MOCVD

A Novel Whisker of α-MoO 3 : Characterization and Growth Mechanism

Preparation of different morphology of TaCx whiskers

Chromium Carbide Micro-Whiskers Dataset: Morphologies with Scanning and Transmission Electronic Microscopy

Rapid and massive growth of tin whisker on mechanochemically decomposed Ti2SnC

Tungsten Oxide Nanowires on Tungsten Substrates

Fabricaion process and growth characteristics of A1N whiskers by sublimation-recrystallization method

Growth mechanism of Y α-SiAlON whiskers prepared by combustion synthesis

Structure Characteristics of AlN Whiskers Fabricated by the Carbo-Thermal Reduction Method

Chromium Carbide Micro-Whiskers: Preparation and Strengthening Effects in Extreme Conditions with Experiments and Molecular Dynamics Simulations

Preparation of Spherical Tungsten Particles Assisted by Hydrothermal Method